LyondellBasell LupolenÂ® 5021 D HDPE, Blow Molding Grade

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer	LyondellBasell
Trade Name	Lupolen®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LyondellBasell LupolenÂ® 5021 D HDPE, Blow Molding Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Easy flow, blow molding grade for small containers (up to 5 l), bottles for surface-active substances, household chemicals, laundry and dishwashing detergents, sanitary cleaners, cosmetics and pharmaceuticals, co-extruded bottles for food and cosmetics.Data was collected by ISO methods and originally provided by BASF. The LupolenÂ® product line is now produced by Basell.

Physical Properties	Metric	English
Density	0.950 g/cc	0.0343 lb/inÂ³
Water Absorption	0.010 %	0.010 %
Moisture Absorption at Equilibrium	0.010 %	0.010 %
Melt Flow	0.265 g/10 min @Load 2.16 kg, Temperature 190 Â°C	0.265 g/10 min @Load 4.76 lb, Temperature 374 Â°F

Mechanical Properties	Metric	English
Tensile Strength, Yield	25.0 MPa	3630 psi
Elongation at Break	>= 50 %	>= 50 %
Elongation at Yield	9.0 %	9.0 %
Tensile Modulus	1.00 GPa	145 ksi
Tensile Impact Strength	130 kJ/mÂ²	61.9 ft-lb/inÂ²
Tensile Creep Modulus, 1 hour	400 MPa	58000 psi
Tensile Creep Modulus, 1000 hours	270 MPa	39200 psi

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	160 Âµm/m-Â°C @Temperature 20.0 Â°C	88.9 Âµin/in-Â°F @Temperature 68.0 Â°F
Melting Point	131 Â°C	268 Â°F
Deflection Temperature at 0.46 MPa (66 psi)	75.0 Â°C	167 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	43.0 Â°C	109 Â°F
Vicat Softening Point	78.0 Â°C	172 Â°F
Flammability, UL94	HB @Thickness 0.400 mm	HB @Thickness 0.0157 in
Oxygen Index	17 %	17 %

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	2.4 @Frequency 100 Hz	2.4 @Frequency 100 Hz
	2.4 @Frequency 1e+6 Hz	2.4 @Frequency 1e+6 Hz
Dielectric Strength	150 kV/mm	3810 kV/in
Dissipation Factor	0.00020 @Frequency 100 Hz	0.00020 @Frequency 100 Hz
	0.00020 @Frequency 1e+6 Hz	0.00020 @Frequency 1e+6 Hz
Comparative Tracking Index	600 V	600 V