LyondellBasell Petrothene® LP510300 High Density Polyethylene

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer LyondellBasell (former Equistar)
Trade Name Petrothene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Petrothene® LP510300 High Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ApplicationsPETROTHENE LLP 5103-00 is a copolymer resin designed for blown film applications. This resin offers high stiffness, excellent appearance and bubble stability and good drawdown. It is recommended for merchandise bags, and multi-wall sack liners and barrier sheeting. It is also useful as a blend component for improved stiffness and machineability.Regulatory StatusLP 5103-00 meets the requirements of Food and Drug Administration regulation 21 CFR 177.1520. This regulation allows the use of this olefin polymer in "…articles or components of articles intended for use in contact with food." Specific limitations or conditions of use may apply. Contact your Equistar sales representative for more information. Processing TechniquesSpecific recommendations for processing LP 5103-00 can only be made when the processing conditions, equipment and end use are known. For further suggestions, please contact your Equistar sales representative. The physical properties are typical values and are not to be construed as specific product limits. Film properties obtained on 1.25 mil film produced using a 2.2:1 blow-up ratio.This product is from the former Equistar product line.
Physical Properties Metric English Comments
Density 0.949 g/cc
0.0343 lb/in³
ASTM D1505
Water Vapor Transmission 6.60 g/m²/day
0.425 g/100 in²/day
ASTM F372
Oxygen Transmission Rate 2900 cc/m²/day
187 cc/100 in²/day
ASTM D3985
Thickness 31.8 microns
1.25 mil
2.2:1 BUR
Melt Flow 0.33 g/10 min
0.33 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 450 %
450 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Dart Drop Test 40.0 g
0.0882 lb
ASTM D1709
Film Tensile Strength at Break, MD 55.2 MPa
8000 psi
ASTM D882
Film Tensile Strength at Break, TD 26.2 MPa
3800 psi
ASTM D882
1% Secant Modulus, MD 772 MPa
112000 psi
1% Secant; ASTM D882
1% Secant Modulus, TD 1100 MPa
160000 psi
1% Secant; ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 126 °C
259 °F
ASTM D1525