LyondellBasell Petrothene® NA942000 Low Density Polyethylene, Film Extrusion Grade

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer LyondellBasell (former Equistar)
Trade Name Petrothene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Petrothene® NA942000 Low Density Polyethylene, Film Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PETROTHENE NA942 is a series of resins designed especially for heavy duty film applications, such as bags used to package fertilizer, peat moss, decorative stone and agricultural and construction materials. NA942 exhibits excellent impact properties and puncture resistance. Regulatory Status: The basic resin NA942 meets the requirements of the Food and Drug Administration regulation, 21 CFR 177.1520. This regulation allows the use of this olefin polymer in "...articles or components of articles intended for use in contact with food." Specific limitations or conditions of use may apply. Contact your Equistar sales representative for further information regarding the suitability of specific products for specific applications.Generally recommended extrusion conditions include a melt temperature range of 330°-430°F (165°- 221°C); a blow-up ratio range of 1.8-2.5:1. Drawdown to 2.0 mils (51 microns) is possible at commercial rates when proper extrusion techniques are used. Specific recommendations for processing NA942 can only be made when the processing conditions, equipment and end use are known. For further suggestions, please contact your Equistar sales representative.This product is from the former Equistar product line.
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
ASTM D1505
ESCR 100% Igepal® 168 hour
168 hour
no failures; molding; ASTM D1693
Thickness 50.8 microns
2.00 mil
Melt Flow 0.18 g/10 min
0.18 g/10 min
ASTM D1238
Antiblock Level 0.000 ppm
0.000 ppm
Slip Level 0.000 ppm
0.000 ppm
Mechanical Properties Metric English Comments
Hardness, Shore D 42
42
molding; ASTM D2240
Tensile Strength at Break 17.9 MPa
2600 psi
molding; ASTM D638
Tensile Strength, Yield 9.65 MPa
1400 psi
molding; ASTM D638
Film Elongation at Break, MD 300 %
300 %
ASTM D882
Film Elongation at Break, TD 450 %
450 %
ASTM D882
Elongation at Break 750 %
750 %
molding; ASTM D638
Elongation at Yield 100 %
100 %
molding; ASTM D638
Dart Drop 4.33 g/micron
110 g/mil
F<sub>50</sub>; ASTM D1709
Film Tensile Strength at Break, MD 20.7 MPa
3000 psi
ASTM D882
Thermal Properties Metric English Comments
Brittleness Temperature <= -75.0 °C
<= -103 °F
F<SUB>50</SUB>; molding; ASTM D746
Processing Properties Metric English Comments
Melt Temperature 221 °C
430 °F
Die Opening 0.0635 cm
0.0250 in
Blow-up Ratio (BUR) 2.0
2.0