LyondellBasell Pro-faxâ„¢ PH350 Polypropylene Homopolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer LyondellBasell
Trade Name Pro-fax™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Pro-faxâ„¢ PH350 Polypropylene Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Pro-faxâ„¢ PH350 general purpose polypropylene homopolymer resin is available as natural flake. Flake form resin is well suited for mixing with pigments and other additives to make polymer concentrates or masterbatches. This resin has very minimal stabilization, which allows wide design latitude for the compounder. Additional suitable stabilization is required to protect the resin during melt processing and throughout its useful life. Pro-faxâ„¢ PH350 flake resin meets FDA requirements in the Code of Federal Regulations, 21 CFR 177.1520, for food contact, including cooking applications. Please note that any additives compounded into this resin will require a re-assessment of its FDA status. All ingredients meet the chemical registration requirements of TSCA (U.S.) and DSL (Canada). Uses: CompoundingInformation provided by Basell.
Physical Properties Metric English Comments
Density 0.902 g/cc
0.0326 lb/in³
ASTM D792
Melt Flow 3.5 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.5 g/10 min

@Load 4.76 lb,
Temperature 446 °F
Condition L; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 85
85
ASTM D 785
Tensile Strength, Yield 33.8 MPa
4900 psi
ASTM D 638
Elongation at Yield 12 %
12 %
ASTM D 638
Flexural Modulus 1.38 GPa
200 ksi
1% Secant, 0.05 in/min; ASTM D790
Izod Impact, Notched 0.374 J/cm
0.700 ft-lb/in
73°F; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Unannealed; ASTM D648