LyondellBasell SEQUEL® E5000 TPO
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | SEQUEL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell SEQUEL® E5000 TPO.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: SEQUEL® E5000 thermoplastic olefinic elastomer (TPO) is designed for extrusion applications that require high mechanical stiffness, thermal stability, good low-temperature properties, and good dimensional stability over a broad temperature range. This material can be supplied with or without UV stabilizers. Applications: Extrusion and thermoforming Information provided by Solvay Engineered Polymers.LyondellBasell acquired Solvay Engineered Polymers in 2008.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | |
| Melt Flow | 0.97 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.97 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | IV, 2 in/min; ASTM D638 |
| Elongation at Break | 223 % | 223 % | ASTM D638 |
| Flexural Modulus | 3.10 GPa | 450 ksi | I.B., TAN, 0.5 in/min; ASTM D790 |
| Izod Impact, Notched | 8.81 J/cm | 16.5 ft-lb/in | NB; ASTM D256 |
| 0.641 J/cm @Temperature -30.0 °C |
1.20 ft-lb/in @Temperature -22.0 °F |
CB; ASTM D256 | |
| Gardner Impact | >= 22.6 J @Temperature -30.0 °C |
>= 16.7 ft-lb @Temperature -22.0 °F |
ASTM D5420-96 |
| 31.6 J @Temperature 23.0 °C |
23.3 ft-lb @Temperature 73.4 °F |
ASTM D5420-96 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 46.8 µm/m-°C @Temperature 20.0 °C |
26.0 µin/in-°F @Temperature 68.0 °F |
modified; ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Synplast™ DUP-E Di Undecyl Phthalate
- Oxford Polymers 802-I Polycarbonate/Polybutylene Terephthalate (PBT) Alloy
- PolyOne Dynaflex™ G7630-9 (Black) Thermoplastic Elastomer (TPE)
- PolyOne Elastamax™ XL-2055 Thermoplastic Polyolefin Elastomer (TPO (POE))
- Quantum Composites QC-3450 48% Glass Fiber High Temperature Use SMC (discontinued **)
- Chase Plastics CP Pryme® NN133LUV (Dry) Nylon 66, 33% Glass Fiber Reinforced, Lubricated, UV Stabilized
- Dow Corning 62 PRINTERS' SOLUTION
- DuPont Teijin Films Mylar® D804 Polyester Film, 92 Gauge
- Asahi Kasei Thermofil N-40MF-0350 40% Mineral Filled, Heat Stabilized
- Asahi Glass Fluon® AH-3000 LM-ETFE, Conductive Type, Fluororesin
Copyright © lookpolymers.com All Rights Reserved