MTI ThermoStran® TPU-40C Long Carbon Fiber Compound

Category Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Carbon Fiber Reinforced
Manufacturer MTI Thermoplastic Composites, Division of Montsinger Technologies, Inc. (MTI)
Trade Name ThermoStran®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF MTI ThermoStran® TPU-40C Long Carbon Fiber Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ThermoStran® is custom designed long fiber thermoplastic compound (LFC) engineered to meet specific end use requirements. Continuous fibers are pultruded to yield pellets with fibers equivalent to the pellet length. Fiber / pellet length = 0.5 inches. Property values are estimated.Processing information:Mold Temperature: Higher mold temperatures are recommended for smoother surface appearance.Nozzle: Shortest length possible and 0.25 inch diameter or larger is recommended.Gates: Gates should be as large as possible and located to eliminate knit line and advantageously align fiber.Runners: Full round runners with 0.25 inch diameter and no sharp corners.Construction Material: Tool steels can be heat treated and polished to increase hardness and wear resistance. A-2 and D-2 steels can be hardened to Rockwell 60 C scale for longer life.Plating: Electroless nickel plating may offer additional wear protection.Information provided by MTI Thermoplastic Composites, Division of Montsinger Technologies, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.37 g/cc
1.37 g/cc
Filler Content 40 %
40 %
Long Carbon Fiber
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 262 MPa
38000 psi
Tensile Modulus 31.0 GPa
4500 ksi
Flexural Strength 379 MPa
55000 psi
Flexural Modulus 27.6 GPa
4000 ksi
Izod Impact, Notched 1.71 J/cm
3.20 ft-lb/in
Processing Properties Metric English Comments
Rear Barrel Temperature 216 °C
420 °F
Middle Barrel Temperature 238 °C
460 °F
Front Barrel Temperature 249 °C
480 °F
Nozzle Temperature 249 °C
480 °F
Melt Temperature 238 - 260 °C
460 - 500 °F
Mold Temperature 65.6 °C
150 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4 hour
4 hour
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 82.7 MPa
12000 psi
Screw Speed 50 - 75 rpm
50 - 75 rpm
Descriptive Properties Value Comments
Nozzle ID 0.25 Inches
Screw Design 20:1 L/D