- Malvern Minerals Nylon with Novakup® L-337 Silane-Treated Quartz Filler
Malvern Minerals Nylon with Novakup® L-337 Silane-Treated Quartz Filler
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Malvern Minerals Company |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Malvern Minerals Nylon with Novakup® L-337 Silane-Treated Quartz Filler.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product data demonstrates the effect of the Novakup® (lamellar quartz surface treated with A-1100) filler. A separate entry demonstrates the effect of untreated Novacite® filler in nylon. The specific nylon used is Huels Nylon 12 L-1901, granulated natural, L-809-0001-0718.Information provided by Malvern Minerals Company.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 44.1 MPa | 6400 psi | after 16 hours in 50°C water |
| 44.8 MPa | 6500 psi | initial | |
| Elongation at Break | 34.6 % | 34.6 % | |
| Flexural Strength | 68.3 MPa | 9900 psi | after 16 hours in 50°C water |
| 77.9 MPa | 11300 psi | initial | |
| Flexural Modulus | 1.45 GPa | 210 ksi | after 16 hours in 50°C water |
| 1.93 GPa | 280 ksi | initial | |
| Izod Impact, Unnotched | 11.9 J/cm | 22.2 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F |