Master Bond EP30-3LO Highly versatile, two part epoxy system for bonding, coating, sealing and casting

Category Polymer , Thermoset , Epoxy , Epoxy Encapsulant, Unreinforced
Manufacturer Master Bond Inc.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Master Bond EP30-3LO Highly versatile, two part epoxy system for bonding, coating, sealing and casting.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Master Bond EP30-3LO is a two component epoxy system featuring a combination of optical clarity and light transmission, good glass transition temperature (Tg), great chemical resistance along with passing NASA low outgassing testing requirements. It has an easy to use 100 to 30 mix ratio by weight, and while it requires heat curing (see below for details) it offers a long open time of 6-10 hours. It bonds well to a wide variety of substrates including metals, glass, composites and many plastics and rubbers. EP30-3LO has good electrical insulation properties and chemical resistance, particularly to water, oils, acids, bases and many solvents. This versatile system can be used for bonding, sealing, coating and potting applications. An added dimension is its compliance with NASA low outgassing requirements. Also ling is its high Tg greater than 175°C, which good for an epoxy with these kinds of optical properties. The service temperature range is -80°F to +450°F. It can be used in aerospace, electronics and most frequently in opto-electronics and optical applications Product Advantages: Convenient mix ratio; 100:30 by weight Low viscosity, easy to apply; very long working life High bonding strength to metals, many plastics, rubber and glass Excellent chemical resistance to acids, bases, oils and solvents Good optical clarity and transmission Outstanding electrical insulation; can be used for potting and encapsulation Resistance to many chemicals including solvents, fuels, acids and bases Bonds well to a wide variety of substratesInformation provided by MasterBond
Physical Properties Metric English Comments
Water Absorption <= 0.10 %

@Temperature 23.9 °C,
Time 86400 sec
<= 0.10 %

@Temperature 75.0 °F,
Time 24.0 hour
Viscosity 100 - 150 cP
100 - 150 cP
Part B
10000 - 14000 cP
10000 - 14000 cP
Part A
Mechanical Properties Metric English Comments
Hardness, Shore D >= 75
>= 75
Tensile Strength at Break >= 75.8 MPa

@Temperature 23.9 °C
>= 11000 psi

@Temperature 75.0 °F
Elongation at Break 4.0 - 5.0 %
4.0 - 5.0 %
Tensile Modulus >= 2.41 GPa

@Temperature 23.9 °C
>= 350 ksi

@Temperature 75.0 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -62.2 °C
-80.0 °F
Glass Transition Temp, Tg >= 175 °C
>= 347 °F
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Dielectric Constant 3.5

@Frequency 60.0 Hz,
Temperature 25.0 °C
3.5

@Frequency 60.0 Hz,
Temperature 77.0 °F
Processing Properties Metric English Comments
Cure Time 60.0 - 120 min

@Temperature 76.7 °C
1.00 - 2.00 hour

@Temperature 170 °F
plus 2-3 hrs at 300°F
Pot Life 3600 - 6000 min
3600 - 6000 min
100 gram mass
Shelf Life 12.0 Month

@Temperature 23.9 °C
12.0 Month

@Temperature 75.0 °F
in original unopened containers
Descriptive Properties Value Comments
Mixing Ratio (A to B) 100:30
by weight