Master Bond Ep46HT-2 Two Component, Heat Resistant Epoxy System

Category Polymer , Thermoset , Epoxy , Epoxy, Cast, Unreinforced , Epoxy, High Temperature
Manufacturer Master Bond Inc.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Master Bond Ep46HT-2 Two Component, Heat Resistant Epoxy System.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Master Bond Polymer System EP46HT-2 is a two component epoxy system for bonding, sealing and casting applications where resistance to temperatures from -100°F to +500°F is required. It is 100% reactive and does not contain any solvents or diluents. It is formulated to cure rapidly and requires a cure temperature of 250°F or more. The glass transition temperature is extremely high, exceeding 220°C. The cured system features exceptional physical and mechanical properties, while exhibiting superior chemical resistance.
Physical Properties Metric English Comments
Viscosity 100 - 200 cP
100 - 200 cP
Part B
12000 - 20000 cP
12000 - 20000 cP
Mixed system
60000 - 110000 cP
60000 - 110000 cP
Part A
Mechanical Properties Metric English Comments
Hardness, Shore D >= 75
>= 75
Tensile Strength >= 68.9 MPa
>= 10000 psi
Elongation at Break 1.0 - 2.0 %
1.0 - 2.0 %
Tensile Modulus >= 2.76 GPa
>= 400 ksi
Compressive Strength >= 138 MPa
>= 20000 psi
Shear Strength >= 17.2 MPa
>= 2500 psi
Tensile, Al/Al
Thermal Properties Metric English Comments
CTE, linear 40.0 - 45.0 µm/m-°C
22.2 - 25.0 µin/in-°F
Maximum Service Temperature, Air 260 °C
500 °F
Minimum Service Temperature, Air -73.3 °C
-100 °F
Glass Transition Temp, Tg >= 220 °C
>= 428 °F
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
Dielectric Strength 17.7 kV/mm

@Thickness 3.17 mm
450 kV/in

@Thickness 0.125 in
Processing Properties Metric English Comments
Cure Time 120 - 180 min

@Temperature 177 - 204 °C
2.00 - 3.00 hour

@Temperature 350 - 400 °F
Post cure (recommended for optimal properties)
180 - 240 min

@Temperature 121 - 149 °C
3.00 - 4.00 hour

@Temperature 250 - 300 °F
Pot Life >= 1440 min
>= 1440 min
100 gram batch
Shelf Life 12.0 Month
12.0 Month
in original unopened containers
Descriptive Properties Value Comments
Mixing Ratio (A to B) 100:35
Parts A to B