Master Bond Supreme 33CLV Two Component, Room Temperature Curing Toughened Epoxy
| Category | Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive |
| Manufacturer | Master Bond Inc. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Master Bond Supreme 33CLV Two Component, Room Temperature Curing Toughened Epoxy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Master Bond Polymer System Supreme 33CLV is a special, room temperature curing, toughened epoxy adhesive/sealant, featuring exceptionally high temperature resistance. This innovative system has outstanding physical properties along with a wide service temperature range from -100°F to +425°F. Supreme 33CLV is a toughened system which imparts superior resistance to impact, thermal shock and thermal cycling. It is 100% reactive and contains no solvents or diluents.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 2500 - 5000 cP | 2500 - 5000 cP | Part B |
| 40000 - 70000 cP | 40000 - 70000 cP | Part A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | >= 75 | >= 75 | |
| Tensile Strength | >= 51.7 MPa | >= 7500 psi | |
| Adhesive Bond Strength | >= 10.3 MPa | >= 1500 psi | Shear, Al/Al, after 30 days at 400°F |
| >= 17.2 MPa | >= 2500 psi | Shear, Al/Al | |
| Peel Strength | >= 2.63 kN/m | >= 15.0 pli |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 218 °C | 425 °F | |
| Minimum Service Temperature, Air | -73.3 °C | -100 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | |
| Dielectric Strength | >= 15.7 kV/mm @Thickness 3.17 mm |
>= 400 kV/in @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 - 180 min @Temperature 93.3 °C |
2.00 - 3.00 hour @Temperature 200 °F |
|
| 2880 - 4320 min @Temperature 23.9 °C |
48.0 - 72.0 hour @Temperature 75.0 °F |
||
| Pot Life | 60 - 90 min | 60 - 90 min | |
| Shelf Life | 12.0 Month | 12.0 Month | original unopened containers |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mixing Ratio (A to B) | 1:1 | by volume |
| 100:70 | by weight |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4945E TPE, Transparent
- Phillips Sumika Marlex® ABF-080 Thermoplastic Polyolefin (discontinued **)
- SABIC Innovative Plastics Cycoloy® C1000HF PC+ABS (Europe-Africa-Middle East)
- Huntsman PE1504 EVA Film Extrusion (discontinued **)
- Wellman Wellamid® GFX1356-BK01 20% Glass Fiber Reinforced, Lubricated Nylon 6
- Braskem H 306 Fiber Extrusion Polypropylene
- Teknor Apex APEX® 2570-H Polyvinyl Chloride, Flexible
- A. Schulman POLYFLAM™ E-15937B High Strength Impact Modified Polypropylene
- Buckeye Polymers BP RPP 2007 TR Blk Reprocessed Polypropylene, 20% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved