Menzolit Menzolit® BMC 1000 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® BMC 1000 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
BMC 1000 is a special BMC for hydrolysis resistant applications. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. Typical applications are components which are exposed to a humid environment. Housings, covers and functional components which are exposed to water or wet atmosphere, like in tropic countries or plant equipment, are typical examples for the use of this material.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 36.0 MPa @Temperature 22.0 °C |
5220 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 36.0 MPa @Temperature 22.0 °C |
5220 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Elongation at Yield | 0.00 % | 0.00 % | tensile rupture strain; ISO 527-4 |
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 120 MPa @Temperature 22.0 °C |
17400 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 10.0 GPa @Temperature 22.0 °C |
1450 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 5.00 GPa | 725 ksi | in plane |
| Charpy Impact, Notched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 150 °C | >= 302 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 125 °C | 257 °F | ISO 11357-2 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Oxygen Index | 22 % | 22 % | ISO 4589-2 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 | 4.0 | IEC 60250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 150 °C | 275 - 302 °F | Injection moulding, matched metal die |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 51 T 25 PP, 25% mineral filling
- SABIC Innovative Plastics Lexan® EXL4016 PC Copolymer (Asia Pacific)
- PolyOne FireCon™ CPE 30-33 RoHS BLACK Polyethylene, Chlorinated (CPE)
- Star Plastics PC7523R Molding Grade PC
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.5 PHR Sulfur
- Teknor Apex Telcar® TL-8730R Thermoplastic Elastomer
- BASF BAPMA N,N-Bis-(3-aminopropyl)methylamine
- Arlon Thermabond® R36300W008 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
- AlphaGary Smokeguard™ LS III 1041 B Low Smoke Polyvinyl Chloride
- Solvay Specialty Polymers Diofan® A610 Polyvinylidene Chloride (PVDC) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved