Menzolit Menzolit® SMC 1400 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass SMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® SMC 1400 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SMC 1400 is a special SMC being used in the environment of a combustion engine. The glass level has been selected to combine good mouldability with good stiffness and strength properties. The product shows an excellent resistance to common fuels, lubricants, cooling liquids and cleaning materials. Because of its specific matrix resin it is suitable for cyclic loads at higher service temperatures. Typical applications are valve covers, camshaft drive covers, gear box covers as well as oil pans or housings for auxiliary drive systems.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | ISO 62 |
| Linear Mold Shrinkage | 0.00030 cm/cm | 0.00030 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 130 MPa @Temperature 22.0 °C |
18900 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 130 MPa @Temperature 22.0 °C |
18900 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Elongation at Yield | 1.6 % | 1.6 % | tensile rupture strain; ISO 527-4 |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 250 MPa @Temperature 22.0 °C |
36300 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 10.0 GPa @Temperature 22.0 °C |
1450 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Compressive Yield Strength | 140 MPa | 20300 psi | ISO 14126 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 3.80 GPa | 551 ksi | in plane |
| Charpy Impact, Notched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.0 µm/m-°C | 6.67 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 162 °C | 324 °F | ISO 11357-2 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Oxygen Index | 22 % | 22 % | ISO 4589-2 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 | 4.0 | IEC 60250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 160 °C | 275 - 320 °F | Compression moulding, matched metal die |
Users viewing this material also viewed the following:
- Overview of materials for Polyphenylene Ether, PTFE Filled
- Schott P-SF67 Glass
- Supreme Petrochem SH 2157 High Impact Polystyrene
- UBE 7034T Nylon 6/12 Monofilament (Drawing Ratio=5, Diameter 0.4 mm)
- A. Schulman POLYFORT™ FPP 1310 Coupled Mica Filled Homopolymer Polypropylene
- Covestro Desmopan® DP 9095AU Polyurethane
- 3M Scotch-Weld™ 847-H Nitrile High Performance Rubber & Gasket Adhesive
- Aremco Ceramabond™ 835-MB High Temperature Ceramic Adhesive/Paste, Alumina Filled
- AlphaGary Evoprene™ GC 5697 SEBS Thermoplastic Elastomer
- Chesterton 989 Release Compound
Copyright © lookpolymers.com All Rights Reserved