Microtherm Group Molded Pipe Sections Filament Reinforced Silica Pipe Insulation

Category Ceramic , Oxide , Silicon Oxide , Other Engineering Material
Manufacturer Microtherm Group
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Microtherm Group Molded Pipe Sections Filament Reinforced Silica Pipe Insulation.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Microtherm® Moulded Pipe Sections (MPS) are preformed pieces of pipe insulation designed to provide a thermally efficient insulation system for piping of all sizes from 25 mm (1”) upwards. Formulation based on pyrogenic silica with a mineral oxide opacifier and E-glass filament reinforcement.PropertiesMicroporous insulation offering the lowest theoretically possible thermal conductivity for continuous operation at temperatures up to to 1000 °C (1832 °F)Precision molded pipe insulation sectionsCan be applied in multi layer systemsNon combustibleEnvironmentally friendlyFree of harmful respirable fibers.Typical ApplicationsAll pipeline applicationsRound ducting applicationsPassive fire protection to piping systems.Information provided by Microtherm.
Physical Properties Metric English Comments
Density 0.320 - 0.350 g/cc
0.0116 - 0.0126 lb/in³
Thickness 25000 microns
984 mil
Mechanical Properties Metric English Comments
Compressive Strength 0.0420 MPa
6.09 psi
Resistance at 10%, 350 kg/m³; ASTM C165
Compressive Modulus 0.00440 GPa
0.638 ksi
@ 350 kg/m³; ASTM C165
Thermal Properties Metric English Comments
Specific Heat Capacity 0.680 J/g-°C

@Temperature 0.000 °C
0.163 BTU/lb-°F

@Temperature 32.0 °F
0.920 J/g-°C

@Temperature 200 °C
0.220 BTU/lb-°F

@Temperature 392 °F
1.00 J/g-°C

@Temperature 400 °C
0.239 BTU/lb-°F

@Temperature 752 °F
1.04 J/g-°C

@Temperature 600 °C
0.249 BTU/lb-°F

@Temperature 1110 °F
1.08 J/g-°C

@Temperature 800 °C
0.258 BTU/lb-°F

@Temperature 1470 °F
Thermal Conductivity 0.0221 W/m-K

@Temperature 100 °C
0.153 BTU-in/hr-ft²-°F

@Temperature 212 °F
@ 320 kg/m³; ASTM C177, ISO 8302
0.0222 W/m-K

@Temperature 200 °C
0.154 BTU-in/hr-ft²-°F

@Temperature 392 °F
@ 320 kg/m³; ASTM C177, ISO 8302
0.0230 W/m-K

@Temperature 300 °C
0.160 BTU-in/hr-ft²-°F

@Temperature 572 °F
@ 320 kg/m³; ASTM C177, ISO 8302
0.0244 W/m-K

@Temperature 400 °C
0.169 BTU-in/hr-ft²-°F

@Temperature 752 °F
@ 320 kg/m³; ASTM C177, ISO 8302
0.0260 W/m-K

@Temperature 500 °C
0.180 BTU-in/hr-ft²-°F

@Temperature 932 °F
@ 320 kg/m³; ASTM C177, ISO 8302
0.0281 W/m-K

@Temperature 600 °C
0.195 BTU-in/hr-ft²-°F

@Temperature 1110 °F
@ 320 kg/m³; ASTM C177, ISO 8302
0.0343 W/m-K

@Temperature 800 °C
0.238 BTU-in/hr-ft²-°F

@Temperature 1470 °F
@ 320 kg/m³; ASTM C177, ISO 8302
Maximum Service Temperature, Air 1000 °C
1830 °F
for long term exposure