Mitsubishi Iupilon® S3000R 16.5 MFI Polycarbonate With Release

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer Mitsubishi
Trade Name Iupilon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsubishi Iupilon® S3000R 16.5 MFI Polycarbonate With Release.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D792
Water Absorption 0.25 %
0.25 %
24 hours at 73°F
Linear Mold Shrinkage 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
ASTM D955
Melt Flow 16.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
16.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
Mechanical Properties Metric English Comments
Hardness, Rockwell M 65
65
ASTM D785
Hardness, Rockwell R 122
122
ASTM D785
Tensile Strength, Ultimate 66.5 MPa

@Thickness 3.17 mm
9650 psi

@Thickness 0.125 in
Tensile Strength, Yield 60.3 MPa

@Thickness 3.17 mm
8750 psi

@Thickness 0.125 in
Elongation at Break 120 %

@Thickness 3.17 mm
120 %

@Thickness 0.125 in
Flexural Yield Strength 85.1 MPa

@Thickness 3.17 mm
12300 psi

@Thickness 0.125 in
Flexural Modulus 2.25 GPa

@Thickness 3.17 mm
326 ksi

@Thickness 0.125 in
Izod Impact, Notched 8.81 J/cm

@Thickness 3.17 mm
16.5 ft-lb/in

@Thickness 0.125 in
Thermal Properties Metric English Comments
CTE, linear 117 µm/m-°C

@Temperature 20.0 °C
65.0 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 128 °C
262 °F
ASTM D648
Flammability, UL94 V-2

@Thickness 1.59 mm
V-2

@Thickness 0.0625 in
Optical Properties Metric English Comments
Refractive Index 1.585
1.585
nD
Transmission, Visible 87 %
87 %
Processing Properties Metric English Comments
Rear Barrel Temperature 249 - 271 °C
480 - 520 °F
Middle Barrel Temperature 260 - 271 °C
500 - 520 °F
Front Barrel Temperature 271 - 288 °C
520 - 550 °F
Nozzle Temperature 266 - 282 °C
510 - 540 °F
Melt Temperature 277 - 293 °C
530 - 560 °F
Mold Temperature 71.1 - 93.3 °C
160 - 200 °F
Drying Temperature 121 °C
250 °F
Dry Time 3 - 4 hour
3 - 4 hour
48 hours max.
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi
Back Pressure 0.345 - 1.38 MPa
50.0 - 200 psi
Clamp Pressure 27.6 - 68.9 MPa
4000 - 10000 psi
Shot Size 40 - 60 %
40 - 60 %
Screw Speed 40 - 70 rpm
40 - 70 rpm
Descriptive Properties Value Comments
Injection Speed- Edge Gate Slow to Medium
Injection Speed- Tab Gate Medium to Fast
Injection Speed- Tunnel Gate Fast