Mitsubishi Xantar® C CM 406 FD C CM 406 Polycarbonate/ABS Blend (European Grade)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Mitsubishi
Trade Name Xantar®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsubishi Xantar® C CM 406 FD C CM 406 Polycarbonate/ABS Blend (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The Xantar® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the Xantar® product line from DSM in 2010.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 0.60 %
0.60 %
Sim. to ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Humidity Absorption; Sim. to ISO 62
Melt Flow 27.12 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 27.12 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 Calculated from Volume Flow Rate of 24 cm<sup>3</sup>/10min.; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 MPa
7250 psi
ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
ISO 527-1/-2
Elongation at Yield 4.0 %
4.0 %
ISO 527-1/-2
Tensile Modulus 2.20 GPa
319 ksi
ISO 527-1/-2
Flexural Strength 80.0 MPa
11600 psi
ISO 178
Flexural Modulus 2.25 GPa
326 ksi
ISO 178
Izod Impact, Notched (ISO) 35.0 kJ/m²

@Temperature -40.0 °C
 16.7 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/4A
55.0 kJ/m²

@Temperature -20.0 °C
 26.2 ft-lb/in²

@Temperature -4.00 °F
 ISO 180/4A
65.0 kJ/m²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/4A
Charpy Impact Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179/1eU
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 2.00 J/cm²

@Temperature -30.0 °C
 9.52 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
4.00 J/cm²

@Temperature 23.0 °C
 19.0 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
ISO 75-1/-2
Vicat Softening Point 120 °C
248 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 IEC 60695-11-10
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 IEC 60695-11-10
Oxygen Index 22 %
22 %
ISO 4589-1/-2
Glow Wire Test 675 °C

@Thickness 1.50 mm
 1250 °F

@Thickness 0.0591 in
 Glow Wire Flammability Index; IEC 60695-2-12
675 °C

@Thickness 1.50 mm
 1250 °F

@Thickness 0.0591 in
 Glow Wire Flammability Index; IEC 60695-2-12
700 °C

@Thickness 1.50 mm
 1290 °F

@Thickness 0.0591 in
 Glow Wire Ignition Temperature; IEC 60695-2-13
700 °C

@Thickness 3.00 mm
 1290 °F

@Thickness 0.118 in
 Glow Wire Ignition Temperature; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 2.9

@Frequency 1e+6 Hz
 2.9

@Frequency 1e+6 Hz
 IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 60243-1
Comparative Tracking Index 275 V
275 V
IEC 60112
250 - 399 V
250 - 399 V
PLC 2; UL 746A
Descriptive Properties Value Comments
High impact or impact modified Yes
Injection molding Yes
Release Agent Yes
Without Fillers Yes