Mitsubishi XantarÂ® SF 22 Polycarbonate

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer	Mitsubishi
Trade Name	Xantar®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Mitsubishi XantarÂ® SF 22 Polycarbonate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

XantarÂ® materials are engineered for performance, consistency and reliability. This makes XantarÂ® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The XantarÂ® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the XantarÂ® product line from DSM in 2010.

Physical Properties	Metric	English	Comments
Density	0.950 g/cc	0.0343 lb/inÂ³	Foamed; ISO 1183
	1.22 g/cc	0.0441 lb/inÂ³	ISO 1183
Water Absorption	0.35 %	0.35 %	Sim. to ISO 62
Viscosity Test	55 cmÂ³/g	55 cmÂ³/g	Limiting Viscosity Number; ISO 1628-4
Melt Flow	6.1 g/10 min @Load 1.20 kg, Temperature 300 Â°C	6.1 g/10 min @Load 2.65 lb, Temperature 572 Â°F	Calculated from Volume Flow Rate of 5 cm<sup>3</sup>/10min.; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	37.0 MPa	5370 psi	ISO 527-1/-2
Elongation at Break	>= 50 %	>= 50 %	ISO 527-1/-2
Elongation at Yield	6.0 %	6.0 %	ISO 527-1/-2
Tensile Modulus	2.00 GPa	290 ksi	ISO 527-1/-2
Flexural Strength	70.0 MPa	10200 psi	ISO 178
Flexural Modulus	2.20 GPa	319 ksi	ISO 178

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	15.0 Âµm/m-Â°C @Temperature 20.0 Â°C	8.33 Âµin/in-Â°F @Temperature 68.0 Â°F	ISO 11359-1/-2
Maximum Service Temperature, Air	125 Â°C	257 Â°F	Ball Pressure Temperature; IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi)	137 Â°C	279 Â°F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	127 Â°C	261 Â°F	ISO 75-1/-2
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in	IEC 60695-11-10
	V-0 @Thickness 6.00 mm	V-0 @Thickness 0.236 in	IEC 60695-11-10
	5VA @Thickness 4.80 mm	5VA @Thickness 0.189 in	IEC 60695-11-20
Oxygen Index	35 %	35 %	ISO 4589-1/-2

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093
Dielectric Constant	3.3 @Frequency 100 Hz	3.3 @Frequency 100 Hz	IEC 60250
	3.3 @Frequency 1e+6 Hz	3.3 @Frequency 1e+6 Hz	IEC 60250
Dissipation Factor	0.00080 @Frequency 100 Hz	0.00080 @Frequency 100 Hz	IEC 60250
	0.0090 @Frequency 1e+6 Hz	0.0090 @Frequency 1e+6 Hz	IEC 60250
Comparative Tracking Index	100 - 174 V	100 - 174 V	PLC 4; UL 746A
	175 V	175 V	IEC 60112

Descriptive Properties	Value	Comments
Flame Retardant	Yes
Flame Retarding Agent	Yes
Heat stabilized or stable to heat	Yes
High impact or impact modified	Yes
Injection molding	Yes
Other Extrusion	Yes
With Fillers	Yes