Mitsui APELâ„¢ APL6509T Cyclo Olefin Copolymer (COC)

Category Polymer , Thermoplastic , Cyclo Olefin Polymer
Manufacturer Mitsui Chemicals America
Trade Name APEL™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsui APELâ„¢ APL6509T Cyclo Olefin Copolymer (COC).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This material possesses many characteristics inherent in polyolefins such as excellent electrical insulating properties and outstanding moisture resistance. In addition, it features good melt processability/flowability, good clarity and transparency, high glass transition temperature (Tg), exceptional moisture impermeability, impressive gas barrier qualities and excellent chemical and heat resistance. This material is used in Film Sheet applications.Information provided by Mitsui Chemicals America, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.02 g/cc
1.02 g/cc
ASTM D792
Moisture Vapor Transmission 0.0900 cc-mm/m²-24hr-atm
0.229 cc-mil/100 in²-24hr-atm
1 atm; ASTM D1249
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
MCI Method
Melt Index of Compound 30 g/10 min

@Load 2.16 kg,
Temperature 260 °C
30 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 MPa
8700 psi
ASTM D638
Elongation at Break 60 %
60 %
ASTM D638
Flexural Strength 100 MPa
14500 psi
ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
ASTM D790
Izod Impact, Notched 0.350 J/cm
0.656 ft-lb/in
ASTM D256
Izod Impact, Unnotched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
ASTM D256
Thermal Properties Metric English Comments
Melting Point 90.0 °C
194 °F
TMA; MCI Method
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
ASTM D648
Glass Transition Temp, Tg 80.0 °C
176 °F
MCI Method
Optical Properties Metric English Comments
Refractive Index 1.54
1.54
ASTM D542
Haze 2.0 %
2.0 %
ASTM D1003
Transmission, Visible 91 %
91 %
ASTM D1003