Mitsui AURUM® JCN3030 Polyimide, Carbon Fiber Filled  (discontinued **)

Category Polymer , Thermoplastic , Polyimide, Thermoplastic
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsui AURUM® JCN3030 Polyimide, Carbon Fiber Filled  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AURUM JCN3030 is a high-performance polyimide for precision injection molded components and extruded products. A member of the AURUM family of advanced engineering resins, carbon fiber reinforced AURUM JCN3030 offers a unique balance of mechanical, thermal, and tribological properties for outstanding performance in demanding automotive, business machinery, industrial equipment, aerospace, and semiconductor equipment applications. AURUM components offer excellent mechanical strength and toughness, dimensional stability, low outgassing, and exceptional radiation resistance. In addition, AURUM exhibits outstanding resistance to hydraulic, automotive, and many industrial fluids and solvents, a low coefficient of thermal expansion, creep resistance, and flame retardancy. AURUM JCN3030 withstands high PV levels and provides a low wear factor and low friction surface over a broad temperature range in both dry and lubricated environments.Applications: AURUM JCN3030 components are excellent replacements for metals, ceramics, and other plastics. High performance AURUM parts include: thrust washers and oil seal rings for automotive and off road vehicle transmissions, thermal insulators and stripper fingers for high-speed copiers, jet engine components, check valve balls, spline couplings, heat-resistant gears, vanes, wear strips, and valve seats. Other AURUM applications include carriers for aluminum hard disks and silicon wafers, journal bearings, and bearing retainers.Information provided by DuPont
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc
1.42 g/cc
ASTM D792
Filler Content 30 %
30 %
Water Absorption 0.23 %
0.23 %
24 hrs @ 73°F; ASTM D570
Linear Mold Shrinkage 0.0025 cm/cm
0.0025 in/in
Melt Flow 27 - 37 g/10 min

@Load 10.0 kg,
Temperature 420 °C
27 - 37 g/10 min

@Load 22.0 lb,
Temperature 788 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 230 MPa
33300 psi
ASTM D638
141 MPa

@Temperature 149 °C
20500 psi

@Temperature 300 °F
ASTM D638
Elongation at Yield 2.0 %
2.0 %
ASTM D638
4.0 %

@Temperature 149 °C
4.0 %

@Temperature 300 °F
ASTM D638
Flexural Strength 314 MPa
45600 psi
ASTM D790
216 MPa

@Temperature 149 °C
31300 psi

@Temperature 300 °F
ASTM D790
Flexural Modulus 17.2 GPa
2500 ksi
ASTM D790
15.2 GPa

@Temperature 149 °C
2200 ksi

@Temperature 300 °F
ASTM D790
Compressive Strength 102 MPa

@Temperature 149 °C
14800 psi

@Temperature 300 °F
JIS K7208
207 MPa

@Temperature 22.8 °C
30000 psi

@Temperature 73.0 °F
JIS K7208
Izod Impact, Notched 1.07 J/cm
2.00 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 5.94 µm/m-°C

@Temperature 20.0 °C
3.30 µin/in-°F

@Temperature 68.0 °F
MD; ASTM D696
46.8 µm/m-°C

@Temperature 20.0 °C
26.0 µin/in-°F

@Temperature 68.0 °F
TD; ASTM D696
Melting Point 388 °C
730 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 248 °C
478 °F
ASTM D648
Glass Transition Temp, Tg 250 °C
482 °F
DSC