Multibase C6-530 Dow-Corning Class VI Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	Multibase
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Multibase C6-530 Dow-Corning Class VI Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Information provided by Multibase

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/inÂ³	Relative, no post cure; ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	30	30	no post cure; ASTM D2240
	31	31	post cured-2 hours at 177Â°C; ASTM D2240
	32	32	post cured-4 hours at 177Â°C; ASTM D2240
	33	33	post cured- 8 hours at 177Â°C; ASTM D2240
Tensile Strength, Ultimate	8.20 MPa	1190 psi	no post cure; ASTM D412
	8.301 MPa	1204 psi	post cured- 8 hours at 177Â°C; ASTM D412
	8.515 MPa	1235 psi	post cured- 4 hours at 177Â°C; ASTM D412
	9.087 MPa	1318 psi	post cured- 2 hours at 177Â°C; ASTM D412
Tensile Strength, Yield	0.889 MPa	129 psi	at 200%, no post cure- press cured for 5 minutes; ASTM D412
	1.05 MPa	152 psi	200%, post cured- 4 hours at 177Â°C; ASTM D412
	1.10 MPa	160 psi	200%, post cured- 8 hours at 177Â°C; ASTM D412
	1.15 MPa	167 psi	at 200%, post cured- 2 hours at 177Â°C; ASTM D412
Elongation at Break	793 %	793 %	post cured- 4 hours at 177Â°C; ASTM D412
	796 %	796 %	post cured- 8 hours at 177Â°C; ASTM D412
	831 %	831 %	no post cure; ASTM D412
	833 %	833 %	post cured- 2 hours at 177Â°C; ASTM D412
Tear Strength	26.3 kN/m	150 pli	Die B, post cured- 4 hours at 177Â°C; ASTM D624
	27.0 kN/m	154 pli	Die B, post cured- 8 hours at 177Â°C; ASTM D624
	27.5 kN/m	157 pli	Die B, no post cure; ASTM D624
	28.2 kN/m	161 pli	Die B,post cured- 2 hours at 177Â°C; ASTM D624
Compression Set	46 %	46 %	no post cure; ASTM D395

Thermal Properties	Metric	English	Comments
Shrinkage	2.0 %	2.0 %	no post cure