Multibase Multi-Flex® TPE A 6821 BLK

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer Multibase
Trade Name Multi-Flex® TPE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase Multi-Flex® TPE A 6821 BLK.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This product is based on Kraton G and PP suitable for automotive applications and meets GM, Ford, and Chrysler specifications. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ASTM D792
Linear Mold Shrinkage 0.014 cm/cm
0.014 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ASTM D955
Melt Flow 10 g/10 min

@Load 5.00 kg,
Temperature 230 °C
10 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Shore A 68
68
10 sec; ASTM D-2240
Tensile Strength, Ultimate >= 5.50 MPa
>= 798 psi
ASTM D638
Elongation at Break >= 1000 %
>= 1000 %
ASTM D638
Flexural Modulus 0.0345 GPa
5.00 ksi
method 1, Proc.B; ASTM D-790
Tear Strength 24.5 kN/m
140 pli
ASTM D624
Compression Set 17 %
17 %
for 70 hours at 23°C; ASTM 395
45 %

@Temperature 70.0 °C
45 %

@Temperature 158 °F
for 70 hours at 70°C; ASTM 395
65 %

@Temperature 100 °C
65 %

@Temperature 212 °F
70 hours at 100°C; ASTM 395