Multibase Multi-Flex® TPE A 8002 BLK

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer Multibase
Trade Name Multi-Flex® TPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase Multi-Flex® TPE A 8002 BLK.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Multi-Flex® TPE 8002 is based on Shell's Kraton G polymer technology and is widely used in the automotive industry for applications requiring elastomeric performance with excellent ozone resistance. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
ASTM D792
Linear Mold Shrinkage 0.013 cm/cm
0.013 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
ASTM D955
Melt Flow 2.0 g/10 min

@Load 5.00 kg,
Temperature 230 °C
2.0 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Shore A 80
80
10 sec; ASTM D-2240
Tensile Strength, Ultimate 11.0 MPa
1600 psi
ASTM D638
Elongation at Break >= 1000 %
>= 1000 %
ASTM D638
Flexural Modulus 0.0345 GPa
5.00 ksi
method 1, Proc.B; ASTM D-790
Tear Strength 51.0 kN/m
291 pli
ASTM D624
Compression Set 22 %
22 %
for 70 hours at 23°C; ASTM 395
55 %

@Temperature 70.0 °C
55 %

@Temperature 158 °F
for 70 hours at 70°C; ASTM 395
76 %

@Temperature 100 °C
76 %

@Temperature 212 °F
70 hours at 100°C; ASTM 395