Multibase Multi-Pro® 2004 R Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Multibase
Trade Name	Multi-Pro®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Multibase Multi-Pro® 2004 R Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Glass Fiber Reinforced, 20% by weight.Features:Heat Resistance, HighScratch ResistantStiffness, GoodForms:PelletsProcessing Methods:Injection MoldingUses:Automotive ApplicationsInformation provided by Multibase

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in³	ASTM D792
Linear Mold Shrinkage	0.0050 cm/cm	0.0050 in/in	ASTM D955
Melt Flow	4.0 g/10 min	4.0 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	44.8 MPa	6500 psi	ASTM D638
Elongation at Break	4.0 %	4.0 %	ASTM D638
Flexural Modulus	3.45 GPa	500 ksi	ASTM D790
Izod Impact, Notched	0.587 J/cm	1.10 ft-lb/in	73°F; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	143 °C	290 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Rear Barrel Temperature	199 - 260 °C	390 - 500 °F
Middle Barrel Temperature	204 - 260 °C	400 - 500 °F
Front Barrel Temperature	216 - 260 °C	420 - 500 °F
Nozzle Temperature	216 - 249 °C	420 - 480 °F
Mold Temperature	4.44 - 65.6 °C	40.0 - 150 °F
Drying Temperature	93.3 °C	200 °F
Dry Time	2 hour	2 hour
Back Pressure	0.138 - 0.345 MPa	20.0 - 50.0 psi
Screw Speed	40 - 100 rpm	40 - 100 rpm

Descriptive Properties	Value	Comments
Clamp Tonnage	2-4 tons/in²
Screw L/D Ratio	20:1