Multibase Multi-Pro® 4003 RC 40% Glass Filled Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Glass Fiber Filler
Manufacturer	Multibase
Trade Name	Multi-Pro®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Multibase Multi-Pro® 4003 RC 40% Glass Filled Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Multi-Pro 4003 RC is a chemically coupled glass reinforced polypropylene compound suitable for engineered plastics applications due to its high heat, flexural and impact properties.Data provided by Multibase.

Physical Properties	Metric	English	Comments
Density	1.24 g/cc	0.0448 lb/in³	ASTM D792-91
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in	ASTM D955-89
Melt Flow	3.0 g/10 min	3.0 g/10 min	(Condition L) ASTM D-1238-94a

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	83	83	10 sec; ASTM D-2240-95
Tensile Strength, Ultimate	79.3 MPa	11500 psi	ASTM D638-95
Elongation at Break	3.0 %	3.0 %	ASTM D638-95
Flexural Strength	75.9 MPa	11000 psi	ASTM D790-95
Flexural Modulus	6.207 GPa	900.3 ksi	Method 1, Proc. B; ASTM D-790-95
Izod Impact, Notched	0.850 J/cm	1.59 ft-lb/in	ASTM D256-93a
Gardner Impact	0.300 J	0.221 ft-lb	ASTM D5420-93

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	164 °C	327 °F	ASTM D648-95
Deflection Temperature at 1.8 MPa (264 psi)	149 °C	300 °F	ASTM D648-95