Mytex Polymers AS319L-01US Thermoplastic Polyolefin, 19% Talc Filled

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin
Manufacturer Mytex Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mytex Polymers AS319L-01US Thermoplastic Polyolefin, 19% Talc Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AS319L-01US is a compounded thermoplastic polyolefin (TPO) designed for exterior automotive applications requiring cold temperature impact, processability and paintability. Available in natural or generic black.Key Applications: Exterior Parts-Bumper Fascia, CladdingOEM Approvals: Chrysler MS-DC 256 Type C, CPN 3338 CP 1120Information provided by Mytex Polymers
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0372 lb/in³
ISO 1183 A
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
48 hours after molding; ISO 294-3/4
0.0060 - 0.0080 cm/cm

@Temperature 80.0 °C,
Time 3600 sec
0.0060 - 0.0080 in/in

@Temperature 176 °F,
Time 1.00 hour
48 hours after molding; ISO 294-3/4
0.0070 - 0.0090 cm/cm

@Temperature 121 °C,
Time 3600 sec
0.0070 - 0.0090 in/in

@Temperature 250 °F,
Time 1.00 hour
48 hours after molding; ISO 294-3/4
Melt Flow 24 g/10 min

@Load 2.16 kg,
Temperature 230 °C
24 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133 B
Ash 19 %

@Temperature 600 °C
19 %

@Temperature 1110 °F
ISO 3451/1A
Mechanical Properties Metric English Comments
Tensile Strength, Yield 17.0 MPa
2470 psi
ISO 527-1/1A/50
Flexural Modulus 1.70 GPa
247 ksi
Chord, 2mm/min; ISO 178
Izod Impact, Unnotched (ISO) 48.0 kJ/m²

@Temperature 23.0 °C
22.8 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1eA
Dart Drop, Total Energy 16.0 J

@Temperature 23.0 °C
11.8 ft-lb

@Temperature 73.4 °F
Multiaxial Impact Strength, Max Load, 2.2 m/s; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 102 °C
216 °F
Method A, flatwise, unannealed; ISO 75-1/2
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
Method A, flatwise, unannealed; ISO 75-1/2