NOVA Chemicals Surpass® HPs167-AB Homopolymer sHDPE Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer NOVA Chemicals
Trade Name Surpass®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Surpass® HPs167-AB Homopolymer sHDPE Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HPs167-AB complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food.NOVA Chemicals' polyethylene resins are biologically and chemically inert.Features: Superior barrier properties, Very high stiffness, Low gelAdditives: AntioxidantApplications: Moisture barrier films, Co-extrusion, Dry food packagingFilm properties are typical of blown film extruded on a 2.5" extruder with 4" die and 35-mil die gap at a blow up ratio of 2:1, but are dependent upon operating conditions.
Physical Properties Metric English Comments
Density 0.966 g/cc
0.0349 lb/in³
ASTM D 792
Moisture Vapor Transmission 0.00418 cc-mm/m²-24hr-atm

@Temperature 38.0 °C
0.0106 cc-mil/100 in²-24hr-atm

@Temperature 100 °F
100% RH; ASTM F 1249
Oxygen Transmission 1.767 cc-mm/m²-24hr-atm
4.488 cc-mil/100 in²-24hr-atm
0% RH; ASTM D 3985
Thickness 38.0 microns
1.50 mil
As tested for properties on this data sheet
25.0 - 75.0 microns
0.984 - 2.95 mil
Recommended range for processing
Melt Flow 1.2 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.2 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 27.0 MPa
3920 psi
ASTM D 882
Film Tensile Strength at Yield, TD 25.0 MPa
3630 psi
ASTM D 882
Elmendorf Tear Strength MD 22 g
22 g
ASTM D 1922
Elmendorf Tear Strength TD 225 g
225 g
ASTM D 1922
Elmendorf Tear Strength, MD 0.580 g/micron
14.7 g/mil
ASTM D 1922
Elmendorf Tear Strength, TD 5.90 g/micron
150 g/mil
ASTM D 1922
1% Secant Modulus, MD 1100 MPa
160000 psi
ASTM D 882
1% Secant Modulus, TD 1335 MPa
193600 psi
ASTM D 882
Processing Properties Metric English Comments
Melt Temperature 200 - 230 °C
392 - 446 °F
Recommended
Die Opening 0.127 - 0.254 cm
0.0500 - 0.100 in
Recommended range
Blow-up Ratio (BUR) 1.5 - 3.0
1.5 - 3.0
Optimum range
Descriptive Properties Value Comments
Low Friction Puncture 19 (J/mm)
NOVA Chemicals test method