NOVA Chemicals Surpass® RMs539-UG Octene sMDPE Rotational Molding Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Rotational Molded
Manufacturer NOVA Chemicals
Trade Name Surpass®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Surpass® RMs539-UG Octene sMDPE Rotational Molding Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Octene copolymerExceptional low temperature impact propertiesOutstanding stiffnessBroad processing windowSuperior whiteness for improved part appearanceEasy mold releaseNSF listed for Standards 14, 24 and 61 Low viscosity for exceptional processability, shorter cycle times, and energy savings Applications: OEM custom and proprietary components Recreational and leisure equipment Marine productsContainers, septic tanks, and fish boxesInformation provided by Nova Chemicals
Physical Properties Metric English Comments
Density 0.939 g/cc
0.0339 lb/in³
Compression Molded; ASTM D792
Environmental Stress Crack Resistance 40 - 50 hour
40 - 50 hour
CTL, Compression Molded; ARM Method
>= 1000 hour
>= 1000 hour
Bent Strip, Compression Molded; ASTM D1693
Melt Flow 5.2 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.2 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Compression Molded; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 61
61
Compression Molded; ASTM D2240
Tensile Strength, Ultimate 27.1 MPa
3930 psi
Compression Molded; ASTM D638
Tensile Strength, Yield 20.0 MPa
2900 psi
Compression Molded; ASTM D638
Elongation at Break 920 %
920 %
Compression Molded; ASTM D638
Elongation at Yield 11 %
11 %
Compression Molded; ASTM D638
Flexural Modulus 0.740 GPa
107 ksi
Compression Molded; ASTM D790
Impact Test 27.0 J

@Thickness 3.17 mm,
Temperature -40.0 °C
19.9 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
Rotational Molded, Instrumented
54.0 J

@Thickness 3.17 mm,
Temperature -40.0 °C
39.8 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
Rotational Molded; ARM Method
108 J

@Thickness 3.17 mm,
Temperature -40.0 °C
79.7 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
Rotational Molded, Instrumented
230 J

@Thickness 3.17 mm,
Temperature -40.0 °C
170 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
Rotational Molded; ARM Method
Thermal Properties Metric English Comments
Melting Point 125 °C
257 °F
Compression Molded; ASTM E794
Deflection Temperature at 0.46 MPa (66 psi) 60.0 °C
140 °F
Compression Molded; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 42.0 °C
108 °F
Compression Molded; ASTM D648
Vicat Softening Point 121 °C
250 °F
Compression Molded; ASTM D1525