NatureWorks® Ingeo™ 3251D Injection Grade PLA

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer	NatureWorks LLC
Trade Name	Ingeo™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NatureWorks® Ingeo™ 3251D Injection Grade PLA.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

IngeoTM Biopolymer 3251D is designed for injection molding applications. This polymer grade has a higher melt flow capability than other IngeoTM resins currently in the market place. The higher flow capability allows for easier molding of thin-walled parts. It is designed for injection molding applications, both clear and opaque, requiring high gloss, UV resistance and stiffness.

Physical Properties	Metric	English	Comments
Specific Gravity	1.24 g/cc	1.24 g/cc	ASTM D792
Viscosity Measurement	2.5	2.5	Relative Viscosity
Linear Mold Shrinkage	0.003 - 0.005 cm/cm	0.003 - 0.005 in/in
Melt Flow	30 - 40 g/10 min @Load 2.16 kg, Temperature 190 °C	30 - 40 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
	70 - 85 g/10 min @Load 2.16 kg, Temperature 210 °C	70 - 85 g/10 min @Load 4.76 lb, Temperature 410 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	48.0 MPa	6960 psi	ASTM D638
Elongation at Break	2.5 %	2.5 %	ASTM D638
Flexural Strength	83.0 MPa	12000 psi	ASTM D790
Izod Impact, Notched	0.160 J/cm	0.300 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	160 - 170 °C	320 - 338 °F	ASTM D3418
Glass Transition Temp, Tg	55.0 - 65.0 °C	131 - 149 °F	ASTM D3417

Optical Properties	Metric	English	Comments
Transmission, Visible	90 %	90 %	Thickness Unknown

Processing Properties	Metric	English
Feed Temperature	166 - 177 °C	331 - 351 °F
Nozzle Temperature	188 - 205 °C	370 - 401 °F
Melt Temperature	188 - 210 °C	370 - 410 °F
Mold Temperature	25.0 °C	77.0 °F
Back Pressure	0.345 - 0.689 MPa	50.0 - 100 psi
Screw Speed	100 - 200 rpm	100 - 200 rpm