NatureWorks® Ingeo™ 4032D Film Grade PLA
| Category | Polymer , Film , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer |
| Manufacturer | NatureWorks LLC |
| Trade Name | Ingeo™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NatureWorks® Ingeo™ 4032D Film Grade PLA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NatureWorks® PLA (polylactide) polymer 4032D can be converted into a biaxially oriented film with use temperatures up to 300°F (150°C). This film has excellent optics, good machinability and excellent twist and deadfold. Additional properties include barrier to flavor and grease and oil resistance. These properties make 4032D film an ideal product for Laminations; Printed films with higher curing temperatures; Other packaging applications.Film properties measured on 1.0 mil film.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D1505 |
| Moisture Vapor Transmission | 8.30 cc-mm/m²-24hr-atm | 21.1 cc-mil/100 in²-24hr-atm | ASTM D1434 |
| Oxygen Transmission | 14.0 cc-mm/m²-24hr-atm | 35.6 cc-mil/100 in²-24hr-atm | ASTM E96 |
| Carbon Dioxide Transmission | 76.0 cc-mm/m²-24hr-atm | 193 cc-mil/100 in²-24hr-atm | ASTM D1434 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 180 % | 180 % | ASTM D882 |
| Film Elongation at Break, TD | 100 % | 100 % | ASTM D882 |
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| Flexural Modulus | 2.85 GPa | 413 ksi | ASTM D790 |
| Secant Modulus, MD | 3.44 GPa | 499 ksi | ASTM D882 |
| Secant Modulus, TD | 3.784 GPa | 548.8 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.669 g/micron | 17.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 0.551 g/micron | 14.0 g/mil | ASTM D1922 |
| Film Tensile Strength at Break, MD | 103.2 MPa | 14970 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 144.5 MPa | 20960 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.1 % | 2.1 % | ASTM D1003 |
| Gloss | 90 % | 90 % | 20°; ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 180 °C | 356 °F | |
| Adapter Temperature | 200 °C | 392 °F | |
| Die Temperature | 200 °C | 392 °F | |
| Melt Temperature | 202 - 218 °C | 396 - 424 °F | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |