NatureWorks® Ingeo™ 8052D Foam Grade Biopolymer
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer |
| Manufacturer | NatureWorks LLC |
| Trade Name | Ingeo™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NatureWorks® Ingeo™ 8052D Foam Grade Biopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ingeo 8052D can be converted into an expanded foam sheet with use temperatures up to 77°F (25°C). This foam is lightweight, strong and suitable for packaging fresh meat and vegetables. In order to extrude foam with the desired expansion properties, this grade must be modified with a branching agent such as Joncryl® 4368C.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Viscosity Measurement | 14 @Temperature 30.0 °C |
14 @Temperature 86.0 °F |
Relative Viscosity; ASTM D5225 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 210 °C |
14 g/10 min @Load 4.76 lb, Temperature 410 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | ASTM D882 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D882 |
| Flexural Strength | 108 MPa | 15700 psi | ASTM D790 |
| Flexural Modulus | 3.55 GPa | 515 ksi | ASTM D790 |
| Izod Impact, Notched | 0.1600 J/cm | 0.2997 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 145 - 160 °C | 293 - 320 °F | Peak; ASTM D3418 |
| Glass Transition Temp, Tg | 55.0 - 60.0 °C | 131 - 140 °F | ASTM D3418 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | Thickness Unknown |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 165 °C | 329 °F | |
| Melt Temperature | 200 °C | 392 °F | |
| Drying Temperature | 75.0 °C @Time 10800 sec |
167 °F @Time 3.00 hour |
|
| Dew Point | -40.0 °C | -40.0 °F | |
| Drying Air Flow Rate | >= 14.2 l/min | >= 0.500 ft³/min (CFM) | |
| Screw Speed | 100 - 175 rpm | 100 - 175 rpm |