Network Polymers Softflex® 3300
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Network Polymers |
| Trade Name | Softflex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers Softflex® 3300.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.868 g/cc | 0.868 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0392 cm/cm @Thickness 3.17 mm |
0.0392 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0392 cm/cm @Thickness 3.17 mm |
0.0392 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 3.4 g/10 min @Load 1.00 kg, Temperature 235 °C |
3.4 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 26 - 36 | 26 - 36 | 10 second dwell; ASTM D2240 |
| 37 - 47 | 37 - 47 | Instantaneous; ASTM D2240 | |
| Tensile Strength at Break | 2.57 MPa | 373 psi | chs 20 in/min; ASTM D412 |
| Elongation at Break | >= 1000 % | >= 1000 % | ASTM D412 |
| 50% Modulus | 0.000560 GPa | 0.0812 ksi | ASTM D412 |
| 100% Modulus | 0.000700 GPa | 0.102 ksi | ASTM D412 |
| 300% Modulus | 0.000960 GPa | 0.139 ksi | ASTM D412 |
| Flexural Modulus | 0.00403 GPa | 0.585 ksi | Test Method I (chs speed 0.5 in/min) |
| Tear Strength | 12.4 kN/m | 70.8 pli | Die C/20"/min; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 0.0013 | 0.0013 | H22 Wheel 1000 g load/1000 cycles; ASTM D3389 |
| Compression Set | 25.9 % | 25.9 % | Method B, 22 hours at 25% deflection and 23°C; ASTM D395 |
| 61.4 % @Temperature 100 °C |
61.4 % @Temperature 212 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
| 72.6 % @Temperature 70.0 °C |
72.6 % @Temperature 158 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
| Tensile Set | 8.6 % | 8.6 % |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE RP 6568 CT BLK
- SABIC Innovative Plastics Lexan® 124 PC (Asia Pacific)
- PolyOne Edgetek® X TR2-10TA/000 NATURAL Copolyester
- SABIC Innovative Plastics LNP THERMOCOMP BFL2200 PC (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOTUF R1000JX4 PA 66 (Asia Pacific)
- A. Schulman POLYFLAM™ FPP 1007 Talc Filled Homopolymer Polypropylene
- Covestro Desmopan® DP 3660DU Polyurethane
- 3M 7660-S-HSG Cold Shrink QT-III Silicone Rubber Skirted Termination Kits
- LATI LARAMID G/30 30% Glass Filled Polyphthalamide (PPA) Based Compound (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved