Nilit Nilamid A G10 FR PH1 50% Glass Fiber Reinforced, Flame Retardant PA66 (with Red Phosphorous)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Nilit |
| Trade Name | Nilamid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit Nilamid A G10 FR PH1 50% Glass Fiber Reinforced, Flame Retardant PA66 (with Red Phosphorous).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Nilamid A G10 FR PH1 was developed specifically for highly loaded, structural applications in the electrical industry. It combines extremely high mechanical performance with flame retardancy. Typical applications include high loaded circuit breaker components, isolator blocks and housings.Key characteristics: Flame retardantExtremely high mechanical performanceHigh CTILow phosphate release Information provided by NILIT.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 0.50 % | 0.50 % | 23°C, 24h in H<sub>2</sub>O; sim. ISO 62 |
| Water Absorption at Saturation | 2.5 % | 2.5 % | sim. ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | Euronil |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | Euronil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 210 MPa | 30500 psi | ISO 527, ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | |
| Tensile Modulus | 15.0 GPa | 2180 ksi | ISO 527, ASTM D638 |
| Flexural Yield Strength | 340 MPa | 49300 psi | ISO 178, ASTM D790 |
| 185 MPa @Temperature 90.0 °C |
26800 psi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Flexural Modulus | 14.0 GPa | 2030 ksi | ISO 178, ASTM D790 |
| 7.00 GPa @Temperature 90.0 °C |
1020 ksi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 13.5 kJ/m² @Temperature 23.0 °C |
6.42 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179 |
| 4.60 J/cm² @Temperature -30.0 °C |
21.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 |
| 0.350 J/cm² @Temperature -30.0 °C |
1.67 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 125 °C | 257 °F | 20,000 hr; IEC 216 |
| Deflection Temperature at 0.46 MPa (66 psi) | 261 °C | 502 °F | ISO 75, ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75, ASTM D648 |
| Vicat Softening Point | 254 °C | 489 °F | 49 N; ISO 306, ASTM D1525 |
| 260 °C | 500 °F | 9.8 N; ISO 306, ASTM D1525 | |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||
| Oxygen Index | 32 % | 32 % | ASTM D2863 |
| Glow Wire Test | 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 21.0 kV/mm @Thickness 2.00 mm |
533 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Comparative Tracking Index | 550 V @Thickness 3.20 mm |
550 V @Thickness 0.126 in |
Sol. A; IEC 112, UL 746A |
| 550 V @Thickness 3.20 mm |
550 V @Thickness 0.126 in |
Sol. B; IEC 112, UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 275 - 285 °C | 527 - 545 °F | |
| Zone 1 | 260 - 280 °C | 500 - 536 °F | hopper |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 270 - 280 °C | 518 - 536 °F | |
| Zone 4 | 275 - 285 °C | 527 - 545 °F | |
| Melt Temperature | 275 - 290 °C | 527 - 554 °F | Do not melt above 290°C |
| Mold Temperature | 90.0 - 110 °C | 194 - 230 °F | Preferred |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamping Force | in tons, 0.7 times the projected surface area in cm2 | |
| Flammability Rating | SE | FMVSS No. 302, 355x100x1 mm |
| Heat Resistance - Ball Test | OK | at 125°C, IEC 309 |
| OK | at 165°C, IEC 309 | |
| Holding Pressure | 90 MPa | |
| Needle Test | OK | IEC 695-2-2, 1 or 2 mm |