Overview of materials for ABS/PVC Alloy

Category	Polymer , Thermoplastic , ABS Polymer , ABS/PVC Alloy , Vinyl (PVC)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Overview of materials for ABS/PVC Alloy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This property data is a summary of similar materials in the MatWeb database for the category "ABS/PVC Alloy". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.

Physical Properties	Metric	English	Comments
Density	0.600 - 1.36 g/cc	0.0217 - 0.0491 lb/in³	Average value: 1.19 g/cc Grade Count:11
Water Absorption	0.0200 - 0.0300 %	0.0200 - 0.0300 %	Average value: 0.0233 % Grade Count:3
Viscosity	190400 - 212400 cP @Temperature 191 - 191 °C	190400 - 212400 cP @Temperature 375 - 375 °F	Average value: 201000 cP Grade Count:2
	190400 - 212400 cP @Shear Rate 3000 - 3000 1/s	190400 - 212400 cP @Shear Rate 3000 - 3000 1/s	Average value: 201000 cP Grade Count:2
Linear Mold Shrinkage	0.00400 - 0.00700 cm/cm	0.00400 - 0.00700 in/in	Average value: 0.00450 cm/cm Grade Count:4
Melt Flow	0.210 - 3.90 g/10 min	0.210 - 3.90 g/10 min	Average value: 1.97 g/10 min Grade Count:3

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	64.0 - 100	64.0 - 100	Average value: 85.7 Grade Count:9
Tensile Strength, Ultimate	9.00 - 50.9 MPa	1310 - 7380 psi	Average value: 34.0 MPa Grade Count:3
Tensile Strength, Yield	31.0 - 40.8 MPa	4500 - 5920 psi	Average value: 34.7 MPa Grade Count:8
Modulus of Elasticity	1.80 - 2.41 GPa	261 - 350 ksi	Average value: 2.09 GPa Grade Count:5
Flexural Yield Strength	17.2 - 75.2 MPa	2490 - 10900 psi	Average value: 54.9 MPa Grade Count:11
Flexural Modulus	1.52 - 2.41 GPa	220 - 350 ksi	Average value: 2.10 GPa Grade Count:10
Izod Impact, Notched	0.900 - 12.5 J/cm	1.69 - 23.4 ft-lb/in	Average value: 5.10 J/cm Grade Count:7
	0.400 - 1.30 J/cm @Temperature -28.9 - -20.0 °C	0.749 - 2.44 ft-lb/in @Temperature -20.0 - -4.00 °F	Average value: 0.854 J/cm Grade Count:5
Izod Impact, Unnotched	0.5339 - 0.5339 J/cm @Temperature -40.0 - -40.0 °C	1.000 - 1.000 ft-lb/in @Temperature -40.0 - -40.0 °F	Average value: 0.534 J/cm Grade Count:1
Falling Dart Impact	27.1164 - 216.931 J @Temperature -40.0 - -40.0 °C	20.0000 - 160.000 ft-lb @Temperature -40.0 - -40.0 °F	Average value: 147 J Grade Count:3

Thermal Properties	Metric	English	Comments
CTE, linear	75.6 - 166 µm/m-°C	42.0 - 92.2 µin/in-°F	Average value: 117 µm/m-°C Grade Count:6
Deflection Temperature at 0.46 MPa (66 psi)	72.0 - 97.0 °C	162 - 207 °F	Average value: 87.2 °C Grade Count:4
Deflection Temperature at 1.8 MPa (264 psi)	66.0 - 82.7 °C	151 - 181 °F	Average value: 74.4 °C Grade Count:11
Vicat Softening Point	70.0 - 80.0 °C	158 - 176 °F	Average value: 76.7 °C Grade Count:3
Flammability, UL94	V-1 - 5VA	V-1 - 5VA	Grade Count:9
Oxygen Index	29.9 - 36.8 %	29.9 - 36.8 %	Average value: 32.0 % Grade Count:4

Electrical Properties	Metric	English	Comments
Surface Resistance	1e+05	1e+05	Grade Count:3