Overview of materials for Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced , Nylon
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Overview of materials for Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.

Physical Properties	Metric	English	Comments
Density	1.09 - 1.53 g/cc	0.0394 - 0.0553 lb/in³	Average value: 1.23 g/cc Grade Count:23
Water Absorption	0.700 - 3.40 %	0.700 - 3.40 %	Average value: 1.18 % Grade Count:13
Moisture Absorption at Equilibrium	0.700 - 1.30 %	0.700 - 1.30 %	Average value: 1.12 % Grade Count:12
Linear Mold Shrinkage	0.00100 - 0.00800 cm/cm	0.00100 - 0.00800 in/in	Average value: 0.00436 cm/cm Grade Count:14
Melt Flow	6.00 - 44.8 g/10 min	6.00 - 44.8 g/10 min	Average value: 20.2 g/10 min Grade Count:9

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	105 - 116	105 - 116	Average value: 112 Grade Count:9
Ball Indentation Hardness	62.0 - 99.0 MPa	8990 - 14400 psi	Average value: 85.3 MPa Grade Count:3
Tensile Strength, Ultimate	31.0 - 128 MPa	4500 - 18500 psi	Average value: 79.1 MPa Grade Count:17
	115 - 115 MPa @Temperature -40.0 - -40.0 °C	16700 - 16700 psi @Temperature -40.0 - -40.0 °F	Average value: 115 MPa Grade Count:1
Tensile Strength, Yield	39.0 - 96.5 MPa	5660 - 14000 psi	Average value: 59.3 MPa Grade Count:10
	37.0 - 37.0 MPa @Temperature 80.0 - 80.0 °C	5370 - 5370 psi @Temperature 176 - 176 °F	Average value: 37.0 MPa Grade Count:1
Elongation at Break	3.00 - 110 %	3.00 - 110 %	Average value: 9.62 % Grade Count:18
	3.30 - 3.30 % @Temperature -40.0 - -40.0 °C	3.30 - 3.30 % @Temperature -40.0 - -40.0 °F	Average value: 3.30 % Grade Count:1
Elongation at Yield	3.00 - 4.00 %	3.00 - 4.00 %	Average value: 3.33 % Grade Count:3
	5.90 - 5.90 % @Temperature 80.0 - 80.0 °C	5.90 - 5.90 % @Temperature 176 - 176 °F	Average value: 5.90 % Grade Count:1
Modulus of Elasticity	2.21 - 7.50 GPa	321 - 1090 ksi	Average value: 3.99 GPa Grade Count:9
Flexural Yield Strength	72.4 - 179 MPa	10500 - 26000 psi	Average value: 120 MPa Grade Count:20
Flexural Modulus	0.597 - 8.13 GPa	86.6 - 1180 ksi	Average value: 4.49 GPa Grade Count:20
Izod Impact, Notched	0.883 - 1.87 J/cm	1.65 - 3.50 ft-lb/in	Average value: 1.38 J/cm Grade Count:14
Izod Impact, Unnotched	9.08 - 5340 J/cm	17.0 - 10000 ft-lb/in	Average value: 9.08 J/cm Grade Count:3
Izod Impact, Notched (ISO)	6.00 - 25.0 kJ/m²	2.86 - 11.9 ft-lb/in²	Average value: 12.8 kJ/m² Grade Count:6
	3.00 - 6.00 kJ/m² @Temperature -30.0 - -30.0 °C	1.43 - 2.86 ft-lb/in² @Temperature -22.0 - -22.0 °F	Average value: 4.67 kJ/m² Grade Count:3
Charpy Impact Unnotched	3.50 - 8.00 J/cm²	16.7 - 38.1 ft-lb/in²	Average value: 5.17 J/cm² Grade Count:6
	2.50 - 4.50 J/cm² @Temperature -30.0 - -30.0 °C	11.9 - 21.4 ft-lb/in² @Temperature -22.0 - -22.0 °F	Average value: 3.75 J/cm² Grade Count:6
Charpy Impact, Notched	0.800 - 2.50 J/cm²	3.81 - 11.9 ft-lb/in²	Average value: 1.40 J/cm² Grade Count:6
	0.300 - 0.700 J/cm² @Temperature -30.0 - -30.0 °C	1.43 - 3.33 ft-lb/in² @Temperature -22.0 - -22.0 °F	Average value: 0.583 J/cm² Grade Count:6

Thermal Properties	Metric	English	Comments
CTE, linear	40.0 - 99.0 µm/m-°C	22.2 - 55.0 µin/in-°F	Average value: 57.4 µm/m-°C Grade Count:7
Deflection Temperature at 0.46 MPa (66 psi)	105 - 215 °C	221 - 419 °F	Average value: 166 °C Grade Count:11
Deflection Temperature at 1.8 MPa (264 psi)	51.7 - 196 °C	125 - 385 °F	Average value: 132 °C Grade Count:19
Vicat Softening Point	108 - 200 °C	226 - 392 °F	Average value: 140 °C Grade Count:6
Flammability, UL94	HB	HB	Grade Count:18

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+11 - 1.00e+15 ohm-cm	1.00e+11 - 1.00e+15 ohm-cm	Average value: 9.17e+13 ohm-cm Grade Count:12
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm	Average value: 1.00e+14 ohm Grade Count:5
Dielectric Constant	2.90 - 5.00	2.90 - 5.00	Average value: 3.48 Grade Count:9
Dielectric Strength	16.5 - 40.0 kV/mm	420 - 1020 kV/in	Average value: 27.6 kV/mm Grade Count:6
Dissipation Factor	0.0130 - 0.0900	0.0130 - 0.0900	Average value: 0.0344 Grade Count:9
Comparative Tracking Index	550 - 600 V	550 - 600 V	Average value: 575 V Grade Count:4

Processing Properties	Metric	English	Comments
Melt Temperature	220 - 270 °C	428 - 518 °F	Average value: 254 °C Grade Count:11
Mold Temperature	40.0 - 90.0 °C	104 - 194 °F	Average value: 68.0 °C Grade Count:5
Injection Velocity	65.0 mm/sec	2.56 in/sec	Average value: 65.0 mm/sec Grade Count:6