Overview of materials for Nylon 12, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, Flame Retardant
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 12, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, Flame Retardant". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.05 - 1.17 g/cc
0.0379 - 0.0423 lb/in³
Average value: 1.07 g/cc Grade Count:7
Moisture Absorption at Equilibrium 0.500 - 0.700 %
0.500 - 0.700 %
Average value: 0.600 % Grade Count:5
Water Absorption at Saturation 1.20 - 1.50 %
1.20 - 1.50 %
Average value: 1.38 % Grade Count:4
Linear Mold Shrinkage 0.00600 - 0.0110 cm/cm
0.00600 - 0.0110 in/in
Average value: 0.00900 cm/cm Grade Count:5
Linear Mold Shrinkage, Transverse 0.00800 - 0.0120 cm/cm
0.00800 - 0.0120 in/in
Average value: 0.0104 cm/cm Grade Count:5
Mechanical Properties Metric English Comments
Tensile Strength, Yield 36.0 - 78.0 MPa
5220 - 11300 psi
Average value: 52.4 MPa Grade Count:7
Elongation at Break 6.00 - 50.0 %
6.00 - 50.0 %
Average value: 44.5 % Grade Count:7
Elongation at Yield 5.00 - 17.0 %
5.00 - 17.0 %
Average value: 7.88 % Grade Count:7
Modulus of Elasticity 1.00 - 2.80 GPa
145 - 406 ksi
Average value: 1.86 GPa Grade Count:7
Charpy Impact Unnotched 3.40 J/cm² - NB
16.2 ft-lb/in² - NB
Average value: 4.95 J/cm² Grade Count:6
3.40 J/cm² - NB

@Temperature -30.0 - 30.0 °C
16.2 ft-lb/in² - NB

@Temperature -22.0 - 86.0 °F
Average value: 5.70 J/cm² Grade Count:5
Charpy Impact, Notched 0.300 - 1.48 J/cm²
1.43 - 7.04 ft-lb/in²
Average value: 0.797 J/cm² Grade Count:6
0.500 - 1.33 J/cm²

@Temperature -30.0 - 30.0 °C
2.38 - 6.33 ft-lb/in²

@Temperature -22.0 - 86.0 °F
Average value: 0.676 J/cm² Grade Count:6
Thermal Properties Metric English Comments
CTE, linear 70.0 - 90.0 µm/m-°C
38.9 - 50.0 µin/in-°F
Average value: 80.0 µm/m-°C Grade Count:4
Melting Point 175 - 178 °C
347 - 352 °F
Average value: 177 °C Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 130 - 160 °C
266 - 320 °F
Average value: 140 °C Grade Count:6
Deflection Temperature at 1.8 MPa (264 psi) 40.0 - 135 °C
104 - 275 °F
Average value: 67.5 °C Grade Count:6
Vicat Softening Point 150 - 175 °C
302 - 347 °F
Average value: 163 °C Grade Count:5
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:7
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 - 1.00e+14 ohm-cm
1.00e+12 - 1.00e+14 ohm-cm
Average value: 5.35e+13 ohm-cm Grade Count:6
Dielectric Constant 3.00 - 7.00
3.00 - 7.00
Average value: 4.53 Grade Count:5
Dielectric Strength 7.00 - 50.0 kV/mm
178 - 1270 kV/in
Average value: 29.0 kV/mm Grade Count:6
Dissipation Factor 0.0200 - 0.170
0.0200 - 0.170
Average value: 0.0588 Grade Count:5
Comparative Tracking Index 175 - 600 V
175 - 600 V
Average value: 518 V Grade Count:6