Overview of materials for Nylon 6, 30% Mineral Filled

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Mineral Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 6, 30% Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.20 - 1.62 g/cc
0.0434 - 0.0585 lb/in³
Average value: 1.38 g/cc Grade Count:81
Water Absorption 0.200 - 8.00 %
0.200 - 8.00 %
Average value: 3.91 % Grade Count:52
Moisture Absorption at Equilibrium 0.170 - 3.00 %
0.170 - 3.00 %
Average value: 1.88 % Grade Count:37
Water Absorption at Saturation 6.00 - 7.50 %
6.00 - 7.50 %
Average value: 6.55 % Grade Count:6
Maximum Moisture Content 0.100
0.100
Average value: 0.100 Grade Count:4
Linear Mold Shrinkage 0.00150 - 0.0190 cm/cm
0.00150 - 0.0190 in/in
Average value: 0.00822 cm/cm Grade Count:64
Linear Mold Shrinkage, Transverse 0.00400 - 0.0189 cm/cm
0.00400 - 0.0189 in/in
Average value: 0.00895 cm/cm Grade Count:28
Melt Flow 3.00 - 81.6 g/10 min
3.00 - 81.6 g/10 min
Average value: 43.7 g/10 min Grade Count:21
Mechanical Properties Metric English Comments
Hardness, Rockwell M 82.0 - 93.0
82.0 - 93.0
Average value: 87.0 Grade Count:5
Hardness, Rockwell R 98.0 - 121
98.0 - 121
Average value: 115 Grade Count:9
Hardness, Shore D 73.0 - 85.0
73.0 - 85.0
Average value: 80.5 Grade Count:4
Ball Indentation Hardness 70.0 - 205 MPa
10200 - 29700 psi
Average value: 151 MPa Grade Count:10
Tensile Strength, Ultimate 30.0 - 128 MPa
4350 - 18500 psi
Average value: 68.4 MPa Grade Count:58
20.0 - 107 MPa

@Temperature -40.0 - 150 °C
2900 - 15500 psi

@Temperature -40.0 - 302 °F
Average value: 40.3 MPa Grade Count:6
Tensile Strength, Yield 30.0 - 103 MPa
4350 - 14900 psi
Average value: 72.4 MPa Grade Count:24
Elongation at Break 1.00 - 70.0 %
1.00 - 70.0 %
Average value: 14.1 % Grade Count:66
3.80 - 35.0 %

@Temperature 60.0 - 150 °C
3.80 - 35.0 %

@Temperature 140 - 302 °F
Average value: 16.2 % Grade Count:2
Elongation at Yield 2.50 - 40.0 %
2.50 - 40.0 %
Average value: 9.84 % Grade Count:9
Modulus of Elasticity 1.64 - 9.00 GPa
238 - 1310 ksi
Average value: 4.66 GPa Grade Count:52
0.443 - 5.622 GPa

@Temperature -20.0 - 150 °C
64.3 - 815.4 ksi

@Temperature -4.00 - 302 °F
Average value: 2.18 GPa Grade Count:3
Flexural Yield Strength 50.0 - 190 MPa
7250 - 27500 psi
Average value: 114 MPa Grade Count:44
53.0 - 168 MPa

@Temperature -40.0 - 80.0 °C
7690 - 24400 psi

@Temperature -40.0 - 176 °F
Average value: 114 MPa Grade Count:1
Flexural Modulus 0.600 - 7.70 GPa
87.0 - 1120 ksi
Average value: 4.41 GPa Grade Count:50
0.800 - 8.00 GPa

@Temperature -40.0 - 120 °C
116 - 1160 ksi

@Temperature -40.0 - 248 °F
Average value: 2.65 GPa Grade Count:4
Izod Impact, Notched 0.250 - 2.60 J/cm
0.468 - 4.87 ft-lb/in
Average value: 0.673 J/cm Grade Count:24
0.200 - 0.680 J/cm

@Temperature -40.0 - -20.0 °C
0.375 - 1.27 ft-lb/in

@Temperature -40.0 - -4.00 °F
Average value: 0.416 J/cm Grade Count:3
Izod Impact, Notched (ISO) 2.60 - 15.0 kJ/m²
1.24 - 7.14 ft-lb/in²
Average value: 7.65 kJ/m² Grade Count:18
4.00 - 8.00 kJ/m²

@Temperature -30.0 - -30.0 °C
1.90 - 3.81 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 5.67 kJ/m² Grade Count:3
Izod Impact, Unnotched (ISO) 35.0 - 35.0 kJ/m²

@Temperature -30.0 - -30.0 °C
16.7 - 16.7 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 35.0 kJ/m² Grade Count:1
Charpy Impact Unnotched 1.30 J/cm² - NB
6.19 ft-lb/in² - NB
Average value: 7.57 J/cm² Grade Count:51
1.30 J/cm² - NB

@Temperature -40.0 - 30.0 °C
6.19 ft-lb/in² - NB

@Temperature -40.0 - 86.0 °F
Average value: 5.41 J/cm² Grade Count:27
Charpy Impact, Notched 0.200 - 1.80 J/cm²
0.952 - 8.57 ft-lb/in²
Average value: 0.701 J/cm² Grade Count:44
0.100 - 1.00 J/cm²

@Temperature -30.0 - 30.0 °C
0.476 - 4.76 ft-lb/in²

@Temperature -22.0 - 86.0 °F
Average value: 0.430 J/cm² Grade Count:22
Tensile Creep Modulus, 1000 hours 740 - 800 MPa
107000 - 116000 psi
Average value: 785 MPa Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 30.0 - 103 µm/m-°C
16.7 - 57.0 µin/in-°F
Average value: 58.5 µm/m-°C Grade Count:30
CTE, linear, Transverse to Flow 40.0 - 102 µm/m-°C
22.2 - 56.7 µin/in-°F
Average value: 61.4 µm/m-°C Grade Count:16
Thermal Conductivity 0.310 W/m-K
2.15 BTU-in/hr-ft²-°F
Average value: 0.310 W/m-K Grade Count:6
Melting Point 210 - 225 °C
410 - 437 °F
Average value: 220 °C Grade Count:61
Maximum Service Temperature, Air 65.0 - 180 °C
149 - 356 °F
Average value: 129 °C Grade Count:18
Deflection Temperature at 0.46 MPa (66 psi) 185 - 240 °C
365 - 464 °F
Average value: 201 °C Grade Count:37
Deflection Temperature at 1.8 MPa (264 psi) 65.0 - 250 °C
149 - 482 °F
Average value: 122 °C Grade Count:64
Deflection Temperature at 8.0 MPa 50.0 °C
122 °F
Average value: 50.0 °C Grade Count:3
Vicat Softening Point 191 - 255 °C
376 - 491 °F
Average value: 207 °C Grade Count:22
Decomposition Temperature 300 °C
572 °F
Average value: 300 °C Grade Count:4
UL RTI, Electrical 65.0 - 140 °C
149 - 284 °F
Average value: 108 °C Grade Count:11
UL RTI, Mechanical with Impact 65.0 - 120 °C
149 - 248 °F
Average value: 90.7 °C Grade Count:11
UL RTI, Mechanical without Impact 65.0 - 140 °C
149 - 284 °F
Average value: 108 °C Grade Count:11
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:59
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+9 - 1.00e+16 ohm-cm
1.00e+9 - 1.00e+16 ohm-cm
Average value: 7.42e+14 ohm-cm Grade Count:41
Surface Resistance 1.00e+10 - 1.00e+16 ohm
1.00e+10 - 1.00e+16 ohm
Average value: 1.45e+15 ohm Grade Count:23
Dielectric Constant 3.00 - 15.0
3.00 - 15.0
Average value: 5.03 Grade Count:18
Dielectric Strength 11.8 - 100 kV/mm
300 - 2540 kV/in
Average value: 29.3 kV/mm Grade Count:24
Dissipation Factor 0.00500 - 0.350
0.00500 - 0.350
Average value: 0.0868 Grade Count:17
Arc Resistance 120 - 185 sec
120 - 185 sec
Average value: 155 sec Grade Count:3
Comparative Tracking Index 250 - 600 V
250 - 600 V
Average value: 475 V Grade Count:43