Overview of materials for Nylon 66, 40% Carbon Fiber Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66, 40% Carbon Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Carbon Fiber Filled". Specific grades with carbon fiber content between 35% and 44% are included.Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.27 - 1.46 g/cc
0.0459 - 0.0527 lb/in³
Average value: 1.32 g/cc Grade Count:15
Filler Content 35.0 - 40.0 %
35.0 - 40.0 %
Average value: 39.3 % Grade Count:7
Water Absorption 0.400 - 2.40 %
0.400 - 2.40 %
Average value: 0.871 % Grade Count:7
Linear Mold Shrinkage 0.000500 - 0.0150 cm/cm
0.000500 - 0.0150 in/in
Average value: 0.00314 cm/cm Grade Count:10
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 200 - 331 MPa
29000 - 48000 psi
Average value: 264 MPa Grade Count:14
105 - 170 MPa

@Temperature 60.0 - 150 °C
15200 - 24700 psi

@Temperature 140 - 302 °F
Average value: 136 MPa Grade Count:1
Elongation at Break 1.00 - 3.00 %
1.00 - 3.00 %
Average value: 1.72 % Grade Count:14
1.80 - 3.20 %

@Temperature 60.0 - 150 °C
1.80 - 3.20 %

@Temperature 140 - 302 °F
Average value: 2.67 % Grade Count:1
Modulus of Elasticity 17.5 - 42.7 GPa
2540 - 6200 ksi
Average value: 28.6 GPa Grade Count:13
8.20 - 23.0 GPa

@Temperature 60.0 - 150 °C
1190 - 3340 ksi

@Temperature 140 - 302 °F
Average value: 14.6 GPa Grade Count:1
Flexural Yield Strength 303 - 483 MPa
44000 - 70100 psi
Average value: 402 MPa Grade Count:13
Flexural Modulus 14.8 - 33.1 GPa
2150 - 4800 ksi
Average value: 22.9 GPa Grade Count:12
Izod Impact, Notched 0.961 - 3.10 J/cm
1.80 - 5.81 ft-lb/in
Average value: 1.78 J/cm Grade Count:11
Izod Impact, Unnotched 6.94 - 11.7 J/cm
13.0 - 22.0 ft-lb/in
Average value: 10.5 J/cm Grade Count:8
Charpy Impact Unnotched 1.80 - 9.50 J/cm²
8.57 - 45.2 ft-lb/in²
Average value: 4.38 J/cm² Grade Count:4
3.00 - 8.00 J/cm²

@Temperature -40.0 - -20.0 °C
14.3 - 38.1 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 4.67 J/cm² Grade Count:3
Charpy Impact, Notched 0.500 - 1.30 J/cm²
2.38 - 6.19 ft-lb/in²
Average value: 0.810 J/cm² Grade Count:4
0.700 - 1.20 J/cm²

@Temperature -30.0 - -20.0 °C
3.33 - 5.71 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 0.950 J/cm² Grade Count:2
Thermal Properties Metric English Comments
CTE, linear 14.4 - 16.2 µm/m-°C
8.00 - 9.00 µin/in-°F
Average value: 14.8 µm/m-°C Grade Count:4
Melting Point 221 - 260 °C
430 - 500 °F
Average value: 246 °C Grade Count:3
Maximum Service Temperature, Air 130 - 140 °C
266 - 284 °F
Average value: 133 °C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 240 - 260 °C
464 - 500 °F
Average value: 255 °C Grade Count:6
Deflection Temperature at 1.8 MPa (264 psi) 230 - 260 °C
446 - 500 °F
Average value: 250 °C Grade Count:14
Flammability, UL94 HB
HB
Grade Count:4
Electrical Properties Metric English Comments
Electrical Resistivity 1.00 ohm-cm - 1e+05
1.00 ohm-cm - 1e+05
Average value: 118 ohm-cm Grade Count:9
Surface Resistance 10.0 - 100 ohm
10.0 - 100 ohm
Average value: 70.0 ohm Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 274 - 293 °C
525 - 560 °F
Average value: 284 °C Grade Count:3
Nozzle Temperature 271 - 304 °C
520 - 580 °F
Average value: 288 °C Grade Count:3
Melt Temperature 260 - 310 °C
500 - 590 °F
Average value: 288 °C Grade Count:6
Mold Temperature 65.6 - 107 °C
150 - 225 °F
Average value: 87.4 °C Grade Count:9
Drying Temperature 79.4 - 100 °C
175 - 212 °F
Average value: 84.9 °C Grade Count:6
Moisture Content 0.150 - 0.200 %
0.150 - 0.200 %
Average value: 0.178 % Grade Count:4
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi
Average value: 96.8 MPa Grade Count:6