Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "PVC, Foam Grade". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.0404 - 1.56 g/cc
0.00146 - 0.0564 lb/in³
Average value: 0.683 g/cc Grade Count:39
Water Absorption 2.40 - 4.00 %
2.40 - 4.00 %
Average value: 3.05 % Grade Count:6
Water Vapor Transmission 0.900 - 7.50 g/m²/day
0.0580 - 0.483 g/100 in²/day
Average value: 4.14 g/m²/day Grade Count:8
Viscosity Test 110 - 200 cm³/g
110 - 200 cm³/g
Average value: 128 cm³/g Grade Count:8
Mechanical Properties Metric English Comments
Hardness, Shore A 42.0 - 80.0
42.0 - 80.0
Average value: 59.2 Grade Count:21
Hardness, Shore OO 13.0 - 45.0
13.0 - 45.0
Average value: 28.7 Grade Count:3
Tensile Strength, Ultimate 0.903 - 20.0 MPa
131 - 2900 psi
Average value: 8.71 MPa Grade Count:24
Tensile Strength, Yield 0.103 - 0.414 MPa
15.0 - 60.0 psi
Average value: 0.317 MPa Grade Count:5
Elongation at Break 1.40 - 450 %
1.40 - 450 %
Average value: 220 % Grade Count:26
Modulus of Elasticity 0.0320 - 1.00 GPa
4.64 - 145 ksi
Average value: 0.302 GPa Grade Count:11
Flexural Yield Strength 12.4 - 33.8 MPa
1800 - 4900 psi
Average value: 26.1 MPa Grade Count:4
Flexural Modulus 1.00 - 1.20 GPa
145 - 174 ksi
Average value: 1.10 GPa Grade Count:3
Compressive Yield Strength 0.00758 - 6.60 MPa
1.10 - 957 psi
Average value: 1.94 MPa Grade Count:13
Compressive Modulus 0.0000138 - 0.600 GPa
0.00200 - 87.0 ksi
Average value: 0.118 GPa Grade Count:14
Poissons Ratio 0.320
0.320
Average value: 0.320 Grade Count:8
Shear Modulus 0.0190 - 0.115 GPa
2.76 - 16.7 ksi
Average value: 0.0472 GPa Grade Count:9
Shear Strength 0.600 - 4.00 MPa
87.0 - 580 psi
Average value: 1.81 MPa Grade Count:9
Izod Impact, Notched 0.210 - 0.540 J/cm
0.393 - 1.01 ft-lb/in
Average value: 0.375 J/cm Grade Count:3
Compression Set 3.20 - 8.00 %
3.20 - 8.00 %
Average value: 5.08 % Grade Count:5
Thermal Properties Metric English Comments
CTE, linear 35.0 - 90.0 µm/m-°C
19.4 - 50.0 µin/in-°F
Average value: 45.1 µm/m-°C Grade Count:11
Specific Heat Capacity 1.13 - 1.90 J/g-°C
0.270 - 0.454 BTU/lb-°F
Average value: 1.57 J/g-°C Grade Count:8
Thermal Conductivity 0.0360 - 0.0432 W/m-K
0.250 - 0.300 BTU-in/hr-ft²-°F
Average value: 0.0399 W/m-K Grade Count:3
0.0230 - 0.0420 W/m-K

@Temperature 10.0 - 10.0 °C
0.160 - 0.291 BTU-in/hr-ft²-°F

@Temperature 50.0 - 50.0 °F
Average value: 0.0311 W/m-K Grade Count:8
Insulation R Value 1.80 - 12.6
1.80 - 12.6
Average value: 5.68 Grade Count:8
Maximum Service Temperature, Air 70.0 - 93.3 °C
158 - 200 °F
Average value: 75.1 °C Grade Count:14
Minimum Service Temperature, Air -200 - -26.1 °C
-328 - -15.0 °F
Average value: -134 °C Grade Count:13
Optical Properties Metric English Comments
Gloss 24.0 - 69.0 %

@Temperature 177 - 199 °C
24.0 - 69.0 %

@Temperature 351 - 390 °F
Average value: 46.5 % Grade Count:1
Processing Properties Metric English Comments
Processing Temperature 80.0 - 129 °C
176 - 264 °F
Average value: 86.1 °C Grade Count:8
Melt Temperature 166 - 188 °C
330 - 370 °F
Average value: 177 °C Grade Count:3