Overview of materials for PVC/Acrylic Alloy

Category Polymer , Thermoplastic , Acrylic (PMMA) , Vinyl (PVC) , PVC/Acrylic Alloy
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for PVC/Acrylic Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "PVC/Acrylic Alloy". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.25 - 1.49 g/cc
0.0452 - 0.0538 lb/in³
Average value: 1.36 g/cc Grade Count:34
Water Absorption 0.0600 - 0.0700 %
0.0600 - 0.0700 %
Average value: 0.0633 % Grade Count:3
Linear Mold Shrinkage 0.00100 - 0.00600 cm/cm
0.00100 - 0.00600 in/in
Average value: 0.00468 cm/cm Grade Count:11
Mechanical Properties Metric English Comments
Hardness, Rockwell R 82.0 - 110
82.0 - 110
Average value: 97.8 Grade Count:27
Tensile Strength, Ultimate 33.0 - 53.0 MPa
4790 - 7690 psi
Average value: 43.6 MPa Grade Count:28
Tensile Strength, Yield 39.3 - 40.7 MPa
5700 - 5900 psi
Average value: 40.1 MPa Grade Count:7
Elongation at Break 55.0 - 195 %
55.0 - 195 %
Average value: 128 % Grade Count:19
Modulus of Elasticity 1.87 - 2.90 GPa
271 - 420 ksi
Average value: 2.36 GPa Grade Count:21
Flexural Yield Strength 44.0 - 76.0 MPa
6380 - 11000 psi
Average value: 66.1 MPa Grade Count:34
Flexural Modulus 2.21 - 3.10 GPa
320 - 449 ksi
Average value: 2.47 GPa Grade Count:15
Izod Impact, Notched 0.320 - 9.60 J/cm
0.599 - 18.0 ft-lb/in
Average value: 5.49 J/cm Grade Count:33
0.500 - 1.0678 J/cm

@Temperature -29.0 - 0.000 °C
0.937 - 2.0004 ft-lb/in

@Temperature -20.2 - 32.0 °F
Average value: 0.784 J/cm Grade Count:2
Taber Abrasion, mg/1000 Cycles 0.0380
0.0380
Average value: 0.0380 Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 38.3 - 101 µm/m-°C
21.3 - 56.0 µin/in-°F
Average value: 79.9 µm/m-°C Grade Count:8
75.6 - 75.6 µm/m-°C

@Temperature 16.0 - 16.0 °C
42.0 - 42.0 µin/in-°F

@Temperature 60.8 - 60.8 °F
Average value: 75.6 µm/m-°C Grade Count:1
Deflection Temperature at 1.8 MPa (264 psi) 65.6 - 82.0 °C
150 - 180 °F
Average value: 74.8 °C Grade Count:34
UL RTI, Electrical 50.0 °C
122 °F
Average value: 50.0 °C Grade Count:4
UL RTI, Mechanical with Impact 50.0 °C
122 °F
Average value: 50.0 °C Grade Count:4
UL RTI, Mechanical without Impact 50.0 °C
122 °F
Average value: 50.0 °C Grade Count:4
Flammability, UL94 V-0 - 5VA
V-0 - 5VA
Grade Count:20
Processing Properties Metric English Comments
Processing Temperature 160 - 200 °C
320 - 392 °F
Average value: 179 °C Grade Count:19
Adapter Temperature 171 - 177 °C
340 - 350 °F
Average value: 174 °C Grade Count:4
Die Temperature 171 - 177 °C
340 - 350 °F
Average value: 174 °C Grade Count:4
Melt Temperature 157 - 207 °C
315 - 405 °F
Average value: 182 °C Grade Count:6