Overview of materials for Phenolic, Novolac, Flock Filled

Category	Polymer , Thermoset , Phenolic , Phenolic, Novolac, Flock Filled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Overview of materials for Phenolic, Novolac, Flock Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Flock Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.

Physical Properties	Metric	English	Comments
Density	1.38 - 1.45 g/cc	0.0499 - 0.0524 lb/in³	Average value: 1.41 g/cc Grade Count:7
Water Absorption	0.180 - 0.630 %	0.180 - 0.630 %	Average value: 0.436 % Grade Count:7
Linear Mold Shrinkage	0.00300 - 0.00850 cm/cm	0.00300 - 0.00850 in/in	Average value: 0.00576 cm/cm Grade Count:7

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell E	63.0 - 91.0	63.0 - 91.0	Average value: 77.7 Grade Count:7
Tensile Strength, Ultimate	36.0 - 55.7 MPa	5220 - 8080 psi	Average value: 48.6 MPa Grade Count:7
Elongation at Break	0.710 - 1.00 %	0.710 - 1.00 %	Average value: 0.817 % Grade Count:6
Modulus of Elasticity	6.90 - 8.27 GPa	1000 - 1200 ksi	Average value: 7.70 GPa Grade Count:6
Flexural Yield Strength	61.0 - 83.2 MPa	8850 - 12100 psi	Average value: 74.2 MPa Grade Count:7
Flexural Modulus	6.20 - 7.72 GPa	899 - 1120 ksi	Average value: 7.12 GPa Grade Count:7
Compressive Yield Strength	139 - 213 MPa	20200 - 30900 psi	Average value: 175 MPa Grade Count:7
Poissons Ratio	0.300 - 0.350	0.300 - 0.350	Average value: 0.338 Grade Count:4
Shear Modulus	2.56 - 3.00 GPa	371 - 435 ksi	Average value: 2.87 GPa Grade Count:4
Izod Impact, Notched	0.210 - 0.277 J/cm	0.393 - 0.519 ft-lb/in	Average value: 0.241 J/cm Grade Count:6
Charpy Impact, Notched	0.199 - 0.400 J/cm²	0.947 - 1.90 ft-lb/in²	Average value: 0.271 J/cm² Grade Count:7

Thermal Properties	Metric	English	Comments
CTE, linear	44.0 - 67.0 µm/m-°C @Temperature 40.0 - 130 °C	24.4 - 37.2 µin/in-°F @Temperature 104 - 266 °F	Average value: 54.0 µm/m-°C Grade Count:3
Thermal Conductivity	0.370 - 0.400 W/m-K @Temperature 100 - 100 °C	2.57 - 2.78 BTU-in/hr-ft²-°F @Temperature 212 - 212 °F	Average value: 0.385 W/m-K Grade Count:2
Maximum Service Temperature, Air	170 - 200 °C	338 - 392 °F	Average value: 189 °C Grade Count:7
Deflection Temperature at 1.8 MPa (264 psi)	156 - 196 °C	313 - 385 °F	Average value: 173 °C Grade Count:7
Flammability, UL94	HB - V-0	HB - V-0	Grade Count:7
Oxygen Index	24.2 - 27.1 %	24.2 - 27.1 %	Average value: 25.7 % Grade Count:3

Electrical Properties	Metric	English	Comments
Electrical Resistivity	6.38e+10 - 2.13e+12 ohm-cm	6.38e+10 - 2.13e+12 ohm-cm	Average value: 5.65e+11 ohm-cm Grade Count:7
Dielectric Constant	4.50 - 6.60	4.50 - 6.60	Average value: 5.14 Grade Count:7
Dielectric Strength	7.90 - 16.2 kV/mm	201 - 411 kV/in	Average value: 11.1 kV/mm Grade Count:7
Dissipation Factor	0.0400 - 0.0760	0.0400 - 0.0760	Average value: 0.0560 Grade Count:7
Arc Resistance	26.0 - 160 sec	26.0 - 160 sec	Average value: 110 sec Grade Count:7
Comparative Tracking Index	150 - 175 V	150 - 175 V	Average value: 168 V Grade Count:7