Overview of materials for Phenolic, Novolac, Mineral/Cellulose Filled

Category Polymer , Thermoset , Phenolic , Phenolic, Novolac, Mineral/Cellulose Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Phenolic, Novolac, Mineral/Cellulose Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Cellulose Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.54 - 1.57 g/cc
0.0556 - 0.0567 lb/in³
Average value: 1.56 g/cc Grade Count:5
Water Absorption 0.163 - 0.224 %
0.163 - 0.224 %
Average value: 0.201 % Grade Count:5
Linear Mold Shrinkage 0.00283 - 0.00760 cm/cm
0.00283 - 0.00760 in/in
Average value: 0.00493 cm/cm Grade Count:5
Mechanical Properties Metric English Comments
Hardness, Rockwell E 77.0 - 84.0
77.0 - 84.0
Average value: 80.2 Grade Count:5
Tensile Strength, Ultimate 44.0 - 55.0 MPa
6380 - 7980 psi
Average value: 50.6 MPa Grade Count:5
Elongation at Break 0.440 - 0.700 %
0.440 - 0.700 %
Average value: 0.596 % Grade Count:5
Modulus of Elasticity 9.90 - 11.3 GPa
1440 - 1640 ksi
Average value: 10.4 GPa Grade Count:5
Flexural Yield Strength 74.0 - 92.0 MPa
10700 - 13300 psi
Average value: 81.2 MPa Grade Count:5
Flexural Modulus 8.60 - 10.5 GPa
1250 - 1520 ksi
Average value: 9.44 GPa Grade Count:5
Compressive Yield Strength 162 - 195 MPa
23500 - 28300 psi
Average value: 177 MPa Grade Count:5
Izod Impact, Notched 0.160 - 0.202 J/cm
0.300 - 0.378 ft-lb/in
Average value: 0.175 J/cm Grade Count:5
Charpy Impact, Notched 0.168 - 0.215 J/cm²
0.800 - 1.02 ft-lb/in²
Average value: 0.195 J/cm² Grade Count:5
Thermal Properties Metric English Comments
CTE, linear 46.0 - 52.0 µm/m-°C

@Temperature 40.0 - 130 °C
25.6 - 28.9 µin/in-°F

@Temperature 104 - 266 °F
Average value: 48.0 µm/m-°C Grade Count:3
Thermal Conductivity 0.540 - 0.540 W/m-K

@Temperature 100 - 100 °C
3.75 - 3.75 BTU-in/hr-ft²-°F

@Temperature 212 - 212 °F
Average value: 0.540 W/m-K Grade Count:2
Maximum Service Temperature, Air 196 - 203 °C
385 - 397 °F
Average value: 201 °C Grade Count:5
Deflection Temperature at 1.8 MPa (264 psi) 173 - 197 °C
343 - 387 °F
Average value: 187 °C Grade Count:5
Flammability, UL94 V-0
V-0
Grade Count:5
Oxygen Index 28.0 - 33.0 %
28.0 - 33.0 %
Average value: 30.7 % Grade Count:3
Electrical Properties Metric English Comments
Electrical Resistivity 3.00e+11 - 3.00e+12 ohm-cm
3.00e+11 - 3.00e+12 ohm-cm
Average value: 1.39e+12 ohm-cm Grade Count:5
Dielectric Constant 5.10 - 5.70
5.10 - 5.70
Average value: 5.40 Grade Count:5
Dielectric Strength 6.60 - 14.9 kV/mm
168 - 378 kV/in
Average value: 11.3 kV/mm Grade Count:5
Dissipation Factor 0.0380 - 0.0740
0.0380 - 0.0740
Average value: 0.0542 Grade Count:5
Arc Resistance 171 - 182 sec
171 - 182 sec
Average value: 178 sec Grade Count:5
Comparative Tracking Index 175 - 200 V
175 - 200 V
Average value: 180 V Grade Count:5