Overview of materials for Polyamide-Imide, Glass Filled

Category Polymer , Thermoplastic , Polyamide-imide (PAI) , Polyamide-Imide, Glass Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyamide-Imide, Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyamide-Imide, Glass Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.58 - 1.61 g/cc
0.0571 - 0.0582 lb/in³
Average value: 1.60 g/cc Grade Count:5
Water Absorption 0.240 - 0.300 %
0.240 - 0.300 %
Average value: 0.280 % Grade Count:3
Water Absorption at Saturation 1.50 - 3.20 %
1.50 - 3.20 %
Average value: 2.07 % Grade Count:3
Mechanical Properties Metric English Comments
Hardness, Rockwell E 85.0 - 90.0
85.0 - 90.0
Average value: 86.7 Grade Count:3
Tensile Strength, Ultimate 103 - 221 MPa
15000 - 32100 psi
Average value: 155 MPa Grade Count:5
Elongation at Break 2.00 - 4.00 %
2.00 - 4.00 %
Average value: 3.00 % Grade Count:4
Modulus of Elasticity 6.21 - 14.5 GPa
900 - 2100 ksi
Average value: 8.50 GPa Grade Count:4
Flexural Yield Strength 138 - 333 MPa
20000 - 48300 psi
Average value: 199 MPa Grade Count:5
181 - 181 MPa

@Temperature 232 - 232 °C
26300 - 26300 psi

@Temperature 450 - 450 °F
Average value: 181 MPa Grade Count:1
Flexural Modulus 5.66 - 11.7 GPa
821 - 1700 ksi
Average value: 7.58 GPa Grade Count:4
9.86 - 9.86 GPa

@Temperature 232 - 232 °C
1430 - 1430 ksi

@Temperature 450 - 450 °F
Average value: 9.86 GPa Grade Count:1
Compressive Yield Strength 55.0 - 276 MPa
7980 - 40000 psi
Average value: 179 MPa Grade Count:4
Compressive Modulus 4.14 - 7.93 GPa
600 - 1150 ksi
Average value: 5.63 GPa Grade Count:3
Izod Impact, Notched 0.374 - 0.800 J/cm
0.700 - 1.50 ft-lb/in
Average value: 0.527 J/cm Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 16.2 - 46.8 µm/m-°C
9.00 - 26.0 µin/in-°F
Average value: 34.0 µm/m-°C Grade Count:4
Thermal Conductivity 0.360 - 0.360 W/m-K
2.50 - 2.50 BTU-in/hr-ft²-°F
Average value: 0.360 W/m-K Grade Count:4
Maximum Service Temperature, Air 250 - 260 °C
482 - 500 °F
Average value: 258 °C Grade Count:4
Deflection Temperature at 1.8 MPa (264 psi) 271 - 282 °C
520 - 540 °F
Average value: 277 °C Grade Count:4
Glass Transition Temp, Tg 275 - 280 °C
527 - 536 °F
Average value: 277 °C Grade Count:3
Flammability, UL94 V-0
V-0
Grade Count:4
Electrical Properties Metric English Comments
Surface Resistance 1.00e+13 - 1.00e+18 ohm
1.00e+13 - 1.00e+18 ohm
Average value: 2.50e+17 ohm Grade Count:4
Dielectric Constant 3.80 - 6.30
3.80 - 6.30
Average value: 4.54 Grade Count:4
Dielectric Strength 17.7 - 33.0 kV/mm
450 - 838 kV/in
Average value: 26.8 kV/mm Grade Count:5
Dissipation Factor 0.00500 - 0.0500
0.00500 - 0.0500
Average value: 0.0233 Grade Count:4