Overview of materials for Polycarbonate/ABS Alloy, Antistat/Conductive

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Antistat/Conductive
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polycarbonate/ABS Alloy, Antistat/Conductive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/ABS Alloy, Antistat/Conductive". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.15 - 1.51 g/cc
0.0415 - 0.0546 lb/in³
Average value: 1.32 g/cc Grade Count:28
Filler Content 5.00 - 20.0 %
5.00 - 20.0 %
Average value: 12.5 % Grade Count:4
Water Absorption 0.100 - 0.120 %
0.100 - 0.120 %
Average value: 0.105 % Grade Count:4
Additive Loading 15.0 - 20.0 %
15.0 - 20.0 %
Average value: 18.3 % Grade Count:3
Linear Mold Shrinkage 0.00100 - 0.00800 cm/cm
0.00100 - 0.00800 in/in
Average value: 0.00455 cm/cm Grade Count:26
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 37.9 - 124 MPa
5500 - 18000 psi
Average value: 66.3 MPa Grade Count:25
Tensile Strength, Yield 54.0 - 58.0 MPa
7830 - 8410 psi
Average value: 56.3 MPa Grade Count:5
Elongation at Break 1.00 - 10.0 %
1.00 - 10.0 %
Average value: 5.61 % Grade Count:27
Elongation at Yield 3.30 - 4.10 %
3.30 - 4.10 %
Average value: 3.57 % Grade Count:3
Modulus of Elasticity 1.72 - 12.1 GPa
250 - 1750 ksi
Average value: 4.35 GPa Grade Count:25
Flexural Yield Strength 55.2 - 193 MPa
8000 - 28000 psi
Average value: 110 MPa Grade Count:28
Flexural Modulus 1.72 - 11.0 GPa
250 - 1600 ksi
Average value: 4.23 GPa Grade Count:28
Izod Impact, Notched 0.374 - 9.61 J/cm
0.700 - 18.0 ft-lb/in
Average value: 1.15 J/cm Grade Count:24
Izod Impact, Unnotched 2.67 - 5340 J/cm
5.00 - 10000 ft-lb/in
Average value: 5.94 J/cm Grade Count:24
Izod Impact, Notched (ISO) 5.00 - 6.00 kJ/m²
2.38 - 2.86 ft-lb/in²
Average value: 5.75 kJ/m² Grade Count:4
Izod Impact, Unnotched (ISO) 35.0 - 43.0 kJ/m²
16.7 - 20.5 ft-lb/in²
Average value: 39.0 kJ/m² Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 39.6 - 77.0 µm/m-°C
22.0 - 42.8 µin/in-°F
Average value: 58.0 µm/m-°C Grade Count:5
CTE, linear, Transverse to Flow 64.0 - 70.0 µm/m-°C
35.6 - 38.9 µin/in-°F
Average value: 66.0 µm/m-°C Grade Count:3
Deflection Temperature at 1.8 MPa (264 psi) 82.0 - 122 °C
180 - 251 °F
Average value: 103 °C Grade Count:12
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:16
Electrical Properties Metric English Comments
Electrical Resistivity 1.00 - 9.90e+10 ohm-cm
1.00 - 9.90e+10 ohm-cm
Average value: 2.22e+9 ohm-cm Grade Count:26
Surface Resistance 1.00 - 9.90e+11 ohm
1.00 - 9.90e+11 ohm
Average value: 2.79e+10 ohm Grade Count:28
Static Decay 0.100 - 2.00 sec
0.100 - 2.00 sec
Average value: 1.18 sec Grade Count:21
Shielding Effectiveness 35.0 - 96.0 dB
35.0 - 96.0 dB
Average value: 70.3 dB Grade Count:5
Processing Properties Metric English Comments
Melt Temperature 216 - 274 °C
420 - 525 °F
Average value: 257 °C Grade Count:22
Mold Temperature 37.8 - 93.3 °C
100 - 200 °F
Average value: 71.0 °C Grade Count:22
Drying Temperature 93.3 °C
200 °F
Average value: 93.3 °C Grade Count:22
Moisture Content 0.0200 %
0.0200 %
Average value: 0.0200 % Grade Count:22
Dew Point -28.9 °C
-20.0 °F
Average value: -28.9 °C Grade Count:22
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:22