Overview of materials for Polyether Ester Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyether Ester Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyether Ester Elastomer". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.05 - 1.48 g/cc
0.0379 - 0.0535 lb/in³
Average value: 1.21 g/cc Grade Count:99
Water Absorption 0.450 - 7.00 %
0.450 - 7.00 %
Average value: 0.993 % Grade Count:57
Moisture Absorption at Equilibrium 0.150 - 0.580 %
0.150 - 0.580 %
Average value: 0.311 % Grade Count:29
Linear Mold Shrinkage 0.00200 - 0.0213 cm/cm
0.00200 - 0.0213 in/in
Average value: 0.0139 cm/cm Grade Count:39
Melt Flow 0.300 - 58.0 g/10 min
0.300 - 58.0 g/10 min
Average value: 13.3 g/10 min Grade Count:92
Mechanical Properties Metric English Comments
Hardness, Shore A 70.0 - 99.0
70.0 - 99.0
Average value: 90.3 Grade Count:4
Hardness, Shore D 20.0 - 80.0
20.0 - 80.0
Average value: 50.4 Grade Count:93
Tensile Strength, Ultimate 7.00 - 57.0 MPa
1020 - 8270 psi
Average value: 27.1 MPa Grade Count:69
Tensile Strength, Yield 1.18 - 35.0 MPa
171 - 5080 psi
Average value: 13.1 MPa Grade Count:65
Elongation at Break 8.50 - 840 %
8.50 - 840 %
Average value: 313 % Grade Count:92
Elongation at Yield 10.0 - 74.0 %
10.0 - 74.0 %
Average value: 31.7 % Grade Count:15
Modulus of Elasticity 0.0500 - 3.07 GPa
7.25 - 445 ksi
Average value: 0.460 GPa Grade Count:35
Tenacity 0.0120 - 0.0250 N/tex
0.136 - 0.283 g/denier
Average value: 0.0187 N/tex Grade Count:10
Flexural Yield Strength 2.26 - 79.0 MPa
327 - 11500 psi
Average value: 20.1 MPa Grade Count:31
Flexural Modulus 0.0150 - 3.09 GPa
2.18 - 448 ksi
Average value: 0.408 GPa Grade Count:63
Compressive Modulus 0.00196 - 0.0350 GPa
0.284 - 5.08 ksi
Average value: 0.0138 GPa Grade Count:4
Resilience 44.0 - 78.0
44.0 - 78.0
Average value: 62.0 Grade Count:4
Izod Impact, Notched 0.686 J/cm - NB
1.29 ft-lb/in - NB
Average value: 2.14 J/cm Grade Count:22
0.490332 - 980.567 J/cm

@Temperature -40.0 - -40.0 °C
0.918594 - 1837.00 ft-lb/in

@Temperature -40.0 - -40.0 °F
Average value: 1.22 J/cm Grade Count:16
0.490332 - 980.567 J/cm

@Thickness 3.17 - 3.17 mm
0.918594 - 1837.00 ft-lb/in

@Thickness 0.125 - 0.125 in
Average value: 1.22 J/cm Grade Count:16
Izod Impact, Unnotched 12.5 J/cm - NB
23.4 ft-lb/in - NB
Average value: 12.5 J/cm Grade Count:3
1.1768 - 980.567 J/cm

@Temperature -40.0 - -23.0 °C
2.2046 - 1837.00 ft-lb/in

@Temperature -40.0 - -9.40 °F
Average value: 3.85 J/cm Grade Count:18
Izod Impact, Notched (ISO) 9.00 kJ/m² - NB
4.28 ft-lb/in² - NB
Average value: 25.4 kJ/m² Grade Count:27
5.00 kJ/m² - NB

@Temperature -40.0 - -20.0 °C
2.38 ft-lb/in² - NB

@Temperature -40.0 - -4.00 °F
Average value: 6.50 kJ/m² Grade Count:13
Charpy Impact Unnotched 0.600 J/cm² - NB

@Temperature -30.0 - -30.0 °C
2.86 ft-lb/in² - NB

@Temperature -22.0 - -22.0 °F
Average value: 0.600 J/cm² Grade Count:3
Charpy Impact, Notched 1.00 J/cm² - NB
4.76 ft-lb/in² - NB
Average value: 2.90 J/cm² Grade Count:32
0.600 J/cm² - NB

@Temperature -30.0 - -30.0 °C
2.86 ft-lb/in² - NB

@Temperature -22.0 - -22.0 °F
Average value: 1.27 J/cm² Grade Count:31
Tensile Impact Strength 179 - 233 kJ/m²
85.2 - 111 ft-lb/in²
Average value: 204 kJ/m² Grade Count:7
Tear Strength 40.0 - 280 kN/m
228 - 1600 pli
Average value: 126 kN/m Grade Count:30
Graves Tear Strength 60.0 - 150 kN/m
342 - 856 pli
Average value: 92.5 kN/m Grade Count:6
Taber Abrasion, mg/1000 Cycles 0.140 - 56.0
0.140 - 56.0
Average value: 29.2 Grade Count:20
Compression Set 50.0 - 60.0 %

@Temperature 70.0 - 70.0 °C
50.0 - 60.0 %

@Temperature 158 - 158 °F
Average value: 55.0 % Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 45.0 - 220 µm/m-°C
25.0 - 122 µin/in-°F
Average value: 143 µm/m-°C Grade Count:24
CTE, linear, Transverse to Flow 110 - 220 µm/m-°C
61.1 - 122 µin/in-°F
Average value: 154 µm/m-°C Grade Count:17
Melting Point 156 - 224 °C
313 - 435 °F
Average value: 203 °C Grade Count:93
Deflection Temperature at 0.46 MPa (66 psi) 46.0 - 187 °C
115 - 369 °F
Average value: 91.5 °C Grade Count:42
Deflection Temperature at 1.8 MPa (264 psi) 47.0 - 170 °C
117 - 338 °F
Average value: 101 °C Grade Count:7
Vicat Softening Point 50.0 - 210 °C
122 - 410 °F
Average value: 145 °C Grade Count:55
Brittleness Temperature -70.0 - -40.0 °C
-94.0 - -40.0 °F
Average value: -61.3 °C Grade Count:30
Glass Transition Temp, Tg -78.0 - -60.0 °C
-108 - -76.0 °F
Average value: -70.0 °C Grade Count:4
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:26
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 - 1.00e+15 ohm-cm
1.00e+12 - 1.00e+15 ohm-cm
Average value: 3.52e+14 ohm-cm Grade Count:19
Surface Resistance 8.00e+10 - 1.00e+15 ohm
8.00e+10 - 1.00e+15 ohm
Average value: 3.39e+14 ohm Grade Count:14
Dielectric Constant 3.30 - 20.0
3.30 - 20.0
Average value: 4.84 Grade Count:15
Dielectric Strength 20.0 - 30.0 kV/mm
508 - 762 kV/in
Average value: 22.1 kV/mm Grade Count:19
Dissipation Factor 0.00100 - 0.0810
0.00100 - 0.0810
Average value: 0.0345 Grade Count:15
Comparative Tracking Index 600 V
600 V
Average value: 600 V Grade Count:19
Processing Properties Metric English Comments
Nozzle Temperature 180 - 220 °C
356 - 428 °F
Average value: 200 °C Grade Count:18
Die Temperature 190 - 220 °C
374 - 428 °F
Average value: 205 °C Grade Count:18
Melt Temperature 170 - 230 °C
338 - 446 °F
Average value: 202 °C Grade Count:18
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Average value: 97.5 °C Grade Count:18
Moisture Content 0.0300 %
0.0300 %
Average value: 0.0300 % Grade Count:18
Injection Pressure 5.90 - 7.90 MPa
856 - 1150 psi
Average value: 6.90 MPa Grade Count:18
Cycle Time - Injection 1.20 - 1.50 sec
1.20 - 1.50 sec
Average value: 1.35 sec Grade Count:18
Cycle Time - Cooling 10.0 - 20.0 sec
10.0 - 20.0 sec
Average value: 15.0 sec Grade Count:18