Overview of materials for Polyetherimide (PEI), 10% Glass Fiber

Category Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), 10% Glass Fiber
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyetherimide (PEI), 10% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 10% Glass Fiber". Specific grades with glass content between 5% and 14% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.30 - 1.69 g/cc
0.0470 - 0.0611 lb/in³
Average value: 1.37 g/cc Grade Count:18
Filler Content 5.00 - 10.0 %
5.00 - 10.0 %
Average value: 9.44 % Grade Count:9
Water Absorption 0.210 - 0.300 %
0.210 - 0.300 %
Average value: 0.244 % Grade Count:13
Linear Mold Shrinkage 0.000500 - 0.00700 cm/cm
0.000500 - 0.00700 in/in
Average value: 0.00476 cm/cm Grade Count:16
Mechanical Properties Metric English Comments
Hardness, Rockwell R 114 - 121
114 - 121
Average value: 119 Grade Count:3
Tensile Strength, Ultimate 68.9 - 138 MPa
10000 - 20000 psi
Average value: 115 MPa Grade Count:15
Tensile Strength, Yield 110 - 121 MPa
16000 - 17500 psi
Average value: 115 MPa Grade Count:5
Elongation at Break 1.00 - 11.0 %
1.00 - 11.0 %
Average value: 4.76 % Grade Count:14
Elongation at Yield 1.30 - 5.00 %
1.30 - 5.00 %
Average value: 3.20 % Grade Count:3
Modulus of Elasticity 4.48 - 11.0 GPa
650 - 1600 ksi
Average value: 6.01 GPa Grade Count:13
Flexural Yield Strength 124 - 214 MPa
18000 - 31000 psi
Average value: 181 MPa Grade Count:17
Flexural Modulus 2.60 - 9.00 GPa
377 - 1310 ksi
Average value: 4.96 GPa Grade Count:18
Compressive Yield Strength 152 MPa
22000 psi
Average value: 152 MPa Grade Count:3
Izod Impact, Notched 0.320 - 0.587 J/cm
0.600 - 1.10 ft-lb/in
Average value: 0.521 J/cm Grade Count:16
Izod Impact, Unnotched 2.14 - 12.8 J/cm
4.00 - 24.0 ft-lb/in
Average value: 6.01 J/cm Grade Count:11
Thermal Properties Metric English Comments
CTE, linear 14.0 - 54.0 µm/m-°C
7.78 - 30.0 µin/in-°F
Average value: 35.3 µm/m-°C Grade Count:8
Thermal Conductivity 0.176 - 0.500 W/m-K
1.22 - 3.47 BTU-in/hr-ft²-°F
Average value: 0.271 W/m-K Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 196 - 223 °C
385 - 433 °F
Average value: 210 °C Grade Count:11
Deflection Temperature at 1.8 MPa (264 psi) 189 - 221 °C
372 - 430 °F
Average value: 206 °C Grade Count:16
Flammability, UL94 V-0
V-0
Grade Count:8
Electrical Properties Metric English Comments
Electrical Resistivity 1000 - 1.00e+17 ohm-cm
1000 - 1.00e+17 ohm-cm
Average value: 2.40e+16 ohm-cm Grade Count:10
Surface Resistance 10000 - 1.00e+12 ohm
10000 - 1.00e+12 ohm
Average value: 3.50e+11 ohm Grade Count:3
Dielectric Constant 3.50 - 3.60
3.50 - 3.60
Average value: 3.55 Grade Count:4
Dielectric Strength 19.7 - 27.6 kV/mm
500 - 700 kV/in
Average value: 22.2 kV/mm Grade Count:6
Dissipation Factor 0.00140 - 0.00500
0.00140 - 0.00500
Average value: 0.00348 Grade Count:4
Processing Properties Metric English Comments
Processing Temperature 349 - 382 °C
660 - 720 °F
Average value: 371 °C Grade Count:8
Nozzle Temperature 343 - 400 °C
649 - 752 °F
Average value: 370 °C Grade Count:4
Melt Temperature 330 - 400 °C
626 - 752 °F
Average value: 364 °C Grade Count:8
Mold Temperature 107 - 180 °C
225 - 356 °F
Average value: 154 °C Grade Count:13
Drying Temperature 120 - 150 °C
248 - 302 °F
Average value: 143 °C Grade Count:8
Moisture Content 0.0200 - 0.0400 %
0.0200 - 0.0400 %
Average value: 0.0350 % Grade Count:4
Dew Point -28.9 °C
-20.0 °F
Average value: -28.9 °C Grade Count:3
Injection Pressure 82.7 - 124 MPa
12000 - 18000 psi
Average value: 103 MPa Grade Count:8