Overview of materials for Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) Alloy, Glass Reinforced, Flow Enhanced". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.29 - 1.70 g/cc
0.0466 - 0.0614 lb/in³
Average value: 1.53 g/cc Grade Count:11
Water Absorption 0.0300 - 0.300 %
0.0300 - 0.300 %
Average value: 0.127 % Grade Count:4
Linear Mold Shrinkage 0.00100 - 0.00500 cm/cm
0.00100 - 0.00500 in/in
Average value: 0.00309 cm/cm Grade Count:11
Linear Mold Shrinkage, Transverse 0.00500 - 0.00600 cm/cm
0.00500 - 0.00600 in/in
Average value: 0.00550 cm/cm Grade Count:4
Spiral Flow 25.0 - 25.0 cm

@Temperature 300 - 300 °C
9.84 - 9.84 in

@Temperature 572 - 572 °F
Average value: 25.0 cm Grade Count:1
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115 - 120
115 - 120
Average value: 119 Grade Count:5
Tensile Strength, Ultimate 112 - 195 MPa
16200 - 28300 psi
Average value: 150 MPa Grade Count:11
Elongation at Break 1.40 - 5.00 %
1.40 - 5.00 %
Average value: 3.03 % Grade Count:11
Flexural Yield Strength 202 - 275 MPa
29300 - 39900 psi
Average value: 224 MPa Grade Count:11
Flexural Modulus 9.30 - 22.0 GPa
1350 - 3190 ksi
Average value: 14.4 GPa Grade Count:11
Compressive Yield Strength 195 - 225 MPa
28300 - 32600 psi
Average value: 211 MPa Grade Count:4
Izod Impact, Notched 0.430 - 1.00 J/cm
0.806 - 1.87 ft-lb/in
Average value: 0.731 J/cm Grade Count:11
Izod Impact, Unnotched 1.60 - 8.00 J/cm
3.00 - 15.0 ft-lb/in
Average value: 4.41 J/cm Grade Count:11
Thermal Properties Metric English Comments
CTE, linear 18.0 - 22.0 µm/m-°C
10.0 - 12.2 µin/in-°F
Average value: 20.0 µm/m-°C Grade Count:4
18.0 - 39.0 µm/m-°C

@Temperature 100 - 200 °C
10.0 - 21.7 µin/in-°F

@Temperature 212 - 392 °F
Average value: 28.5 µm/m-°C Grade Count:4
CTE, linear, Transverse to Flow 50.0 - 63.0 µm/m-°C
27.8 - 35.0 µin/in-°F
Average value: 56.5 µm/m-°C Grade Count:4
92.0 - 110 µm/m-°C

@Temperature 100 - 200 °C
51.1 - 61.1 µin/in-°F

@Temperature 212 - 392 °F
Average value: 101 µm/m-°C Grade Count:4
Melting Point 280 - 290 °C
536 - 554 °F
Average value: 284 °C Grade Count:6
Deflection Temperature at 0.46 MPa (66 psi) 250 - 271 °C
482 - 520 °F
Average value: 261 °C Grade Count:6
Deflection Temperature at 1.8 MPa (264 psi) 229 - 260 °C
444 - 500 °F
Average value: 246 °C Grade Count:11
Flammability, UL94 V-0
V-0
Grade Count:3
Electrical Properties Metric English Comments
Dielectric Constant 3.80 - 4.50
3.80 - 4.50
Average value: 4.05 Grade Count:5
Dielectric Strength 17.0 - 27.0 kV/mm
432 - 686 kV/in
Average value: 23.0 kV/mm Grade Count:5
Dissipation Factor 0.00200 - 0.0300
0.00200 - 0.0300
Average value: 0.0136 Grade Count:5
Arc Resistance 100 - 116 sec
100 - 116 sec
Average value: 108 sec Grade Count:4
Comparative Tracking Index 150 - 275 V
150 - 275 V
Average value: 225 V Grade Count:5
Processing Properties Metric English Comments
Melt Temperature 299 - 330 °C
570 - 626 °F
Average value: 308 °C Grade Count:6