Overview of materials for Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Carbon Fiber Filler". Specific grades with carbon fiber content between 15% and 24% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.39 - 1.54 g/cc
0.0502 - 0.0556 lb/in³
Average value: 1.44 g/cc Grade Count:22
Filler Content 15.0 - 40.0 %
15.0 - 40.0 %
Average value: 22.3 % Grade Count:13
Additive Loading 15.0 - 20.0 %
15.0 - 20.0 %
Average value: 17.0 % Grade Count:5
Linear Mold Shrinkage 0.000200 - 0.00200 cm/cm
0.000200 - 0.00200 in/in
Average value: 0.00110 cm/cm Grade Count:17
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 27.6 - 186 MPa
4000 - 27000 psi
Average value: 139 MPa Grade Count:22
45.0 - 135 MPa

@Temperature 60.0 - 150 °C
6530 - 19600 psi

@Temperature 140 - 302 °F
Average value: 86.3 MPa Grade Count:2
Elongation at Break 0.300 - 2.50 %
0.300 - 2.50 %
Average value: 1.20 % Grade Count:23
1.10 - 2.30 %

@Temperature 60.0 - 150 °C
1.10 - 2.30 %

@Temperature 140 - 302 °F
Average value: 1.71 % Grade Count:2
Modulus of Elasticity 8.27 - 26.2 GPa
1200 - 3800 ksi
Average value: 17.4 GPa Grade Count:19
7.20 - 16.0 GPa

@Temperature 60.0 - 150 °C
1040 - 2320 ksi

@Temperature 140 - 302 °F
Average value: 11.7 GPa Grade Count:2
Flexural Yield Strength 53.1 - 262 MPa
7700 - 38000 psi
Average value: 195 MPa Grade Count:21
Flexural Modulus 8.27 - 19.3 GPa
1200 - 2800 ksi
Average value: 14.8 GPa Grade Count:20
Izod Impact, Notched 0.347 - 1.98 J/cm
0.650 - 3.71 ft-lb/in
Average value: 0.626 J/cm Grade Count:18
Izod Impact, Unnotched 2.19 - 4.27 J/cm
4.10 - 8.00 ft-lb/in
Average value: 3.36 J/cm Grade Count:14
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 200 - 232 °C
392 - 450 °F
Average value: 217 °C Grade Count:3
Deflection Temperature at 0.46 MPa (66 psi) 260 - 280 °C
500 - 536 °F
Average value: 274 °C Grade Count:4
Deflection Temperature at 1.8 MPa (264 psi) 235 - 270 °C
455 - 518 °F
Average value: 262 °C Grade Count:17
Flammability, UL94 V-0
V-0
Grade Count:15
Electrical Properties Metric English Comments
Electrical Resistivity 100 - 1.00e+6 ohm-cm
100 - 1.00e+6 ohm-cm
Average value: 117000 ohm-cm Grade Count:15
Surface Resistance 10.0 - 1.00e+7 ohm
10.0 - 1.00e+7 ohm
Average value: 2.59e+6 ohm Grade Count:12
Processing Properties Metric English Comments
Melt Temperature 205 - 345 °C
401 - 653 °F
Average value: 316 °C Grade Count:17
Mold Temperature 130 - 177 °C
266 - 350 °F
Average value: 153 °C Grade Count:18
Drying Temperature 120 - 150 °C
248 - 302 °F
Average value: 145 °C Grade Count:16
Moisture Content 0.0400 %
0.0400 %
Average value: 0.0400 % Grade Count:12
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi
Average value: 88.6 MPa Grade Count:14