Overview of materials for Polyphenylene Sulfide (PPS) with PTFE Filler

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with PTFE Filler
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphenylene Sulfide (PPS) with PTFE Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with PTFE Filler". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.34 - 2.03 g/cc
0.0484 - 0.0733 lb/in³
Average value: 1.54 g/cc Grade Count:23
Filler Content 10.0 - 70.0 %
10.0 - 70.0 %
Average value: 35.5 % Grade Count:19
Water Absorption 0.0200 - 0.200 %
0.0200 - 0.200 %
Average value: 0.130 % Grade Count:4
Linear Mold Shrinkage 0.00200 - 0.0200 cm/cm
0.00200 - 0.0200 in/in
Average value: 0.0118 cm/cm Grade Count:15
Mechanical Properties Metric English Comments
Hardness, Shore D 64.0 - 89.0
64.0 - 89.0
Average value: 77.2 Grade Count:6
Tensile Strength, Ultimate 11.0 - 75.8 MPa
1600 - 11000 psi
Average value: 41.7 MPa Grade Count:25
Elongation at Break 0.500 - 68.0 %
0.500 - 68.0 %
Average value: 4.37 % Grade Count:23
Modulus of Elasticity 1.65 - 9.65 GPa
240 - 1400 ksi
Average value: 4.09 GPa Grade Count:21
Flexural Yield Strength 18.6 - 117 MPa
2700 - 17000 psi
Average value: 70.4 MPa Grade Count:24
Flexural Modulus 1.31 - 10.3 GPa
190 - 1500 ksi
Average value: 4.09 GPa Grade Count:21
Compressive Yield Strength 24.1 - 100 MPa
3500 - 14500 psi
Average value: 49.0 MPa Grade Count:4
Izod Impact, Notched 0.160 - 0.854 J/cm
0.300 - 1.60 ft-lb/in
Average value: 0.344 J/cm Grade Count:16
Izod Impact, Unnotched 1.07 - 3.74 J/cm
2.00 - 7.00 ft-lb/in
Average value: 2.14 J/cm Grade Count:11
Charpy Impact Unnotched 1.00 - 2.00 J/cm²
4.76 - 9.52 ft-lb/in²
Average value: 1.50 J/cm² Grade Count:3
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 93.0 - 232 °C
199 - 450 °F
Average value: 133 °C Grade Count:13
Flammability, UL94 V-0
V-0
Grade Count:11
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 - 1.00e+16 ohm-cm
1.00e+14 - 1.00e+16 ohm-cm
Average value: 2.80e+15 ohm-cm Grade Count:4
Surface Resistance 10000 - 1.00e+15 ohm
10000 - 1.00e+15 ohm
Average value: 2.50e+14 ohm Grade Count:4
Processing Properties Metric English Comments
Processing Temperature 288 - 330 °C
550 - 626 °F
Average value: 321 °C Grade Count:3
Melt Temperature 288 - 343 °C
550 - 650 °F
Average value: 318 °C Grade Count:14
Mold Temperature 130 - 180 °C
266 - 356 °F
Average value: 155 °C Grade Count:15
Drying Temperature 50.0 - 150 °C
122 - 302 °F
Average value: 130 °C Grade Count:14
Moisture Content 0.0400 %
0.0400 %
Average value: 0.0400 % Grade Count:7
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:11