Overview of materials for Polypropylene, Flame Retardant

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polypropylene, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Flame Retardant". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.850 - 1.90 g/cc
0.0307 - 0.0686 lb/in³
Average value: 1.09 g/cc Grade Count:250
Filler Content 10.0 - 40.0 %
10.0 - 40.0 %
Average value: 23.7 % Grade Count:18
Water Absorption 0.0100 - 0.0500 %
0.0100 - 0.0500 %
Average value: 0.0227 % Grade Count:49
Maximum Moisture Content 0.0100 - 0.0200
0.0100 - 0.0200
Average value: 0.0125 Grade Count:4
Linear Mold Shrinkage 0.000100 - 0.0500 cm/cm
0.000100 - 0.0500 in/in
Average value: 0.0144 cm/cm Grade Count:176
Linear Mold Shrinkage, Transverse 0.00700 - 0.0243 cm/cm
0.00700 - 0.0243 in/in
Average value: 0.0164 cm/cm Grade Count:29
Melt Flow 0.300 - 140 g/10 min
0.300 - 140 g/10 min
Average value: 12.4 g/10 min Grade Count:170
Ash 15.0 - 25.0 %
15.0 - 25.0 %
Average value: 20.0 % Grade Count:4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100
100
Average value: 100 Grade Count:4
Hardness, Rockwell R 69.0 - 105
69.0 - 105
Average value: 89.7 Grade Count:20
Hardness, Shore A 66.0 - 69.0
66.0 - 69.0
Average value: 67.8 Grade Count:6
Hardness, Shore D 60.0 - 80.0
60.0 - 80.0
Average value: 71.0 Grade Count:30
Tensile Strength, Ultimate 10.3 - 300 MPa
1500 - 43500 psi
Average value: 31.7 MPa Grade Count:167
7.00 - 45.0 MPa

@Temperature 60.0 - 90.0 °C
1020 - 6530 psi

@Temperature 140 - 194 °F
Average value: 16.9 MPa Grade Count:4
Tensile Strength, Yield 2.07 - 75.0 MPa
300 - 10900 psi
Average value: 27.9 MPa Grade Count:100
Elongation at Break 1.00 - 558 %
1.00 - 558 %
Average value: 64.0 % Grade Count:182
4.00 - 20.0 %

@Temperature 60.0 - 90.0 °C
4.00 - 20.0 %

@Temperature 140 - 194 °F
Average value: 66.2 % Grade Count:8
Elongation at Yield 2.00 - 350 %
2.00 - 350 %
Average value: 31.6 % Grade Count:46
2.50 - 10.0 %

@Temperature 60.0 - 90.0 °C
2.50 - 10.0 %

@Temperature 140 - 194 °F
Average value: 7.56 % Grade Count:8
Modulus of Elasticity 0.800 - 9.31 GPa
116 - 1350 ksi
Average value: 2.08 GPa Grade Count:120
0.300 - 5.70 GPa

@Temperature 60.0 - 90.0 °C
43.5 - 827 ksi

@Temperature 140 - 194 °F
Average value: 1.26 GPa Grade Count:8
Flexural Yield Strength 17.9 - 300 MPa
2600 - 43500 psi
Average value: 40.5 MPa Grade Count:128
Flexural Modulus 0.621 - 7.24 GPa
90.0 - 1050 ksi
Average value: 1.79 GPa Grade Count:199
Izod Impact, Notched 0.107 J/cm - NB
0.200 ft-lb/in - NB
Average value: 0.913 J/cm Grade Count:165
0.150 - 0.550 J/cm

@Temperature -20.0 - 0.000 °C
0.281 - 1.03 ft-lb/in

@Temperature -4.00 - 32.0 °F
Average value: 0.329 J/cm Grade Count:17
Izod Impact, Unnotched 0.801 - 5340 J/cm
1.50 - 10000 ft-lb/in
Average value: 8.47 J/cm Grade Count:46
Izod Impact, Notched (ISO) 2.00 - 60.0 kJ/m²
0.952 - 28.6 ft-lb/in²
Average value: 7.59 kJ/m² Grade Count:44
2.00 - 10.0 kJ/m²

@Temperature -30.0 - -20.0 °C
0.952 - 4.76 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 4.11 kJ/m² Grade Count:9
Izod Impact, Unnotched (ISO) 15.0 - 98.0 kJ/m²
7.14 - 46.6 ft-lb/in²
Average value: 56.2 kJ/m² Grade Count:10
13.0 - 13.0 kJ/m²

@Temperature -30.0 - -30.0 °C
6.19 - 6.19 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 13.0 kJ/m² Grade Count:1
Charpy Impact Unnotched 1.00 J/cm² - NB
4.76 ft-lb/in² - NB
Average value: 4.21 J/cm² Grade Count:48
0.650 - 999.9 J/cm²

@Temperature -40.0 - -20.0 °C
3.09 - 4759 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 3.16 J/cm² Grade Count:26
Charpy Impact, Notched 0.150 - 9.00 J/cm²
0.714 - 42.8 ft-lb/in²
Average value: 0.657 J/cm² Grade Count:53
0.0400 - 1.40 J/cm²

@Temperature -30.0 - -20.0 °C
0.190 - 6.66 ft-lb/in²

@Temperature -22.0 - -4.00 °F
Average value: 0.266 J/cm² Grade Count:30
Gardner Impact 0.904 - 260 J
0.667 - 192 ft-lb
Average value: 26.8 J Grade Count:24
Dart Drop, Total Energy 2.71 - 14.9 J
2.00 - 11.0 ft-lb
Average value: 8.59 J Grade Count:3
Dart Drop Total Energy 1.44 - 8.54 J/cm
0.00270 - 0.0160 ft-lb/mil
Average value: 6.10 J/cm Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 31.0 - 120 µm/m-°C
17.2 - 66.7 µin/in-°F
Average value: 69.8 µm/m-°C Grade Count:10
CTE, linear, Transverse to Flow 96.0 - 140 µm/m-°C
53.3 - 77.8 µin/in-°F
Average value: 116 µm/m-°C Grade Count:4
Thermal Conductivity 0.170 - 0.303 W/m-K
1.18 - 2.10 BTU-in/hr-ft²-°F
Average value: 0.258 W/m-K Grade Count:3
Melting Point 130 - 170 °C
266 - 338 °F
Average value: 162 °C Grade Count:52
Maximum Service Temperature, Air 60.0 - 130 °C
140 - 266 °F
Average value: 92.7 °C Grade Count:14
Deflection Temperature at 0.46 MPa (66 psi) 70.0 - 187 °C
158 - 368 °F
Average value: 109 °C Grade Count:119
Deflection Temperature at 1.8 MPa (264 psi) 40.6 - 155 °C
105 - 311 °F
Average value: 68.4 °C Grade Count:152
Electrical Properties Metric English Comments
Electrical Resistivity 10.0 - 1.00e+17 ohm-cm
10.0 - 1.00e+17 ohm-cm
Average value: 4.60e+15 ohm-cm Grade Count:80
Surface Resistance 1000 - 1.00e+16 ohm
1000 - 1.00e+16 ohm
Average value: 2.31e+15 ohm Grade Count:45
Static Decay 0.500 - 2.00 sec
0.500 - 2.00 sec
Average value: 1.50 sec Grade Count:3
Dielectric Constant 2.10 - 3.06
2.10 - 3.06
Average value: 2.50 Grade Count:9
Dielectric Strength 17.7 - 43.0 kV/mm
450 - 1090 kV/in
Average value: 28.8 kV/mm Grade Count:50
Dissipation Factor 0.00120 - 0.0100
0.00120 - 0.0100
Average value: 0.00380 Grade Count:4
Arc Resistance 60.0 - 180 sec
60.0 - 180 sec
Average value: 124 sec Grade Count:6
Comparative Tracking Index 350 - 600 V
350 - 600 V
Average value: 552 V Grade Count:52
Hot Wire Ignition, HWI 7.00 - 60.0 sec
7.00 - 60.0 sec
Average value: 26.8 sec Grade Count:4
High Amp Arc Ignition, HAI 120 arcs
120 arcs
Average value: 120 arcs Grade Count:4
High Voltage Arc-Tracking Rate, HVTR 0.000 - 330 mm/min
0.000 - 13.0 in/min
Average value: 116 mm/min Grade Count:3