Overview of materials for Polypropylene, Wood Filled

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Wood Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polypropylene, Wood Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Wood Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.951 - 1.21 g/cc
0.0344 - 0.0437 lb/in³
Average value: 1.03 g/cc Grade Count:22
Linear Mold Shrinkage 0.00180 - 0.0100 cm/cm
0.00180 - 0.0100 in/in
Average value: 0.00549 cm/cm Grade Count:14
Melt Flow 0.500 - 7.40 g/10 min
0.500 - 7.40 g/10 min
Average value: 2.65 g/10 min Grade Count:12
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 20.0 - 62.1 MPa
2900 - 9000 psi
Average value: 36.6 MPa Grade Count:16
Tensile Strength, Yield 21.0 - 40.0 MPa
3050 - 5800 psi
Average value: 28.4 MPa Grade Count:9
Elongation at Break 1.20 - 10.0 %
1.20 - 10.0 %
Average value: 5.18 % Grade Count:20
Modulus of Elasticity 1.72 - 6.20 GPa
250 - 899 ksi
Average value: 3.26 GPa Grade Count:20
Flexural Yield Strength 38.0 - 103 MPa
5510 - 15000 psi
Average value: 57.6 MPa Grade Count:19
Flexural Modulus 1.79 - 4.90 GPa
260 - 711 ksi
Average value: 2.96 GPa Grade Count:21
Izod Impact, Notched 0.220 - 0.801 J/cm
0.412 - 1.50 ft-lb/in
Average value: 0.471 J/cm Grade Count:18
Izod Impact, Unnotched 0.400 - 5.34 J/cm
0.749 - 10.0 ft-lb/in
Average value: 3.00 J/cm Grade Count:18
Thermal Properties Metric English Comments
CTE, linear 36.0 - 63.0 µm/m-°C
20.0 - 35.0 µin/in-°F
Average value: 49.7 µm/m-°C Grade Count:6
Deflection Temperature at 0.46 MPa (66 psi) 65.6 - 142 °C
150 - 288 °F
Average value: 122 °C Grade Count:10
Deflection Temperature at 1.8 MPa (264 psi) 60.0 - 128 °C
140 - 262 °F
Average value: 78.0 °C Grade Count:18
Processing Properties Metric English Comments
Processing Temperature 200 °C
392 °F
Average value: 200 °C Grade Count:8
Melt Temperature 185 - 232 °C
365 - 450 °F
Average value: 203 °C Grade Count:13
Mold Temperature 30.0 - 65.6 °C
86.0 - 150 °F
Average value: 47.4 °C Grade Count:12
Drying Temperature 70.0 - 90.0 °C
158 - 194 °F
Average value: 78.4 °C Grade Count:13
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:10