Overview of materials for Polypropylene with 20% Talc Filler

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polypropylene with 20% Talc Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Talc Filler".Specific grades with primary filler content between 15% and 24% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.980 - 1.46 g/cc
0.0354 - 0.0527 lb/in³
Average value: 1.05 g/cc Grade Count:296
Filler Content 15.0 - 25.0 %
15.0 - 25.0 %
Average value: 19.3 % Grade Count:153
Water Absorption 0.0200 - 0.0300 %
0.0200 - 0.0300 %
Average value: 0.0277 % Grade Count:13
Linear Mold Shrinkage 0.000900 - 0.0265 cm/cm
0.000900 - 0.0265 in/in
Average value: 0.0120 cm/cm Grade Count:236
Linear Mold Shrinkage, Transverse 0.00720 - 0.0272 cm/cm
0.00720 - 0.0272 in/in
Average value: 0.0153 cm/cm Grade Count:31
Melt Flow 0.600 - 30.0 g/10 min
0.600 - 30.0 g/10 min
Average value: 12.6 g/10 min Grade Count:268
Ash 16.0 - 25.0 %
16.0 - 25.0 %
Average value: 20.4 % Grade Count:20
15.0 - 20.0 %

@Temperature 600 - 600 °C
15.0 - 20.0 %

@Temperature 1110 - 1110 °F
Average value: 19.0 % Grade Count:5
Mechanical Properties Metric English Comments
Hardness, Rockwell M 48.0 - 100
48.0 - 100
Average value: 67.8 Grade Count:4
Hardness, Rockwell R 52.0 - 98.0
52.0 - 98.0
Average value: 86.8 Grade Count:38
Hardness, Shore D 56.0 - 80.0
56.0 - 80.0
Average value: 69.5 Grade Count:66
Tensile Strength, Ultimate 12.0 - 37.0 MPa
1740 - 5370 psi
Average value: 26.8 MPa Grade Count:212
Tensile Strength, Yield 13.8 - 39.0 MPa
2000 - 5660 psi
Average value: 28.4 MPa Grade Count:105
Elongation at Break 3.00 - 400 %
3.00 - 400 %
Average value: 30.7 % Grade Count:125
Elongation at Yield 3.00 - 32.0 %
3.00 - 32.0 %
Average value: 8.70 % Grade Count:125
Modulus of Elasticity 1.10 - 3.45 GPa
160 - 500 ksi
Average value: 2.19 GPa Grade Count:85
Flexural Yield Strength 17.0 - 70.0 MPa
2470 - 10200 psi
Average value: 42.9 MPa Grade Count:163
Flexural Modulus 1.02 - 4.10 GPa
148 - 595 ksi
Average value: 2.08 GPa Grade Count:301
2.30 - 2.40 GPa

@Temperature -20.0 - -20.0 °C
334 - 348 ksi

@Temperature -4.00 - -4.00 °F
Average value: 2.32 GPa Grade Count:5
Izod Impact, Notched 0.198 - 8.01 J/cm
0.370 - 15.0 ft-lb/in
Average value: 0.688 J/cm Grade Count:159
0.200 - 0.26695 J/cm

@Temperature -40.0 - -20.0 °C
0.375 - 0.50011 ft-lb/in

@Temperature -40.0 - -4.00 °F
Average value: 0.229 J/cm Grade Count:3
Izod Impact, Unnotched 0.200 - 5340 J/cm
0.375 - 10000 ft-lb/in
Average value: 5.80 J/cm Grade Count:44
Izod Impact, Notched (ISO) 2.40 - 28.0 kJ/m²
1.14 - 13.3 ft-lb/in²
Average value: 8.43 kJ/m² Grade Count:14
1.80 - 4.00 kJ/m²

@Temperature -40.0 - -20.0 °C
0.857 - 1.90 ft-lb/in²

@Temperature -40.0 - -4.00 °F
Average value: 2.41 kJ/m² Grade Count:7
Izod Impact, Unnotched (ISO) 15.0 - 55.0 kJ/m²
7.14 - 26.2 ft-lb/in²
Average value: 31.3 kJ/m² Grade Count:4
17.0 - 24.0 kJ/m²

@Temperature -30.0 - -30.0 °C
8.09 - 11.4 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 20.5 kJ/m² Grade Count:2
Charpy Impact Unnotched 1.50 J/cm² - NB
7.14 ft-lb/in² - NB
Average value: 4.92 J/cm² Grade Count:68
1.00 J/cm² - NB

@Temperature -30.0 - 0.000 °C
4.76 ft-lb/in² - NB

@Temperature -22.0 - 32.0 °F
Average value: 2.55 J/cm² Grade Count:63
Charpy Impact, Notched 0.200 - 7.50 J/cm²
0.952 - 35.7 ft-lb/in²
Average value: 1.07 J/cm² Grade Count:127
0.100 - 4.80 J/cm²

@Temperature -40.0 - 0.000 °C
0.476 - 22.8 ft-lb/in²

@Temperature -40.0 - 32.0 °F
Average value: 0.394 J/cm² Grade Count:108
Gardner Impact 0.451 - 271 J
0.333 - 200 ft-lb
Average value: 13.4 J Grade Count:74
1.35582 - 43.3862 J

@Temperature -30.0 - -5.56 °C
1.00000 - 32.0000 ft-lb

@Temperature -22.0 - 22.0 °F
Average value: 13.7 J Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 50.0 - 110 µm/m-°C
27.8 - 61.1 µin/in-°F
Average value: 68.2 µm/m-°C Grade Count:24
Melting Point 135 - 182 °C
275 - 360 °F
Average value: 157 °C Grade Count:26
Deflection Temperature at 0.46 MPa (66 psi) 70.0 - 144 °C
158 - 291 °F
Average value: 114 °C Grade Count:233
Deflection Temperature at 1.8 MPa (264 psi) 25.0 - 174 °C
77.0 - 345 °F
Average value: 71.4 °C Grade Count:236
Vicat Softening Point 53.0 - 160 °C
127 - 320 °F
Average value: 113 °C Grade Count:112
Flammability, UL94 HB - 5VA
HB - 5VA
Grade Count:100
Flame Spread 15.2 - 22.9 mm/min
0.600 - 0.900 in/min
Average value: 19.8 mm/min Grade Count:5
Glow Wire Test 650 - 960 °C
1200 - 1760 °F
Average value: 746 °C Grade Count:52
Optical Properties Metric English Comments
Gloss 45.0 - 47.0 %
45.0 - 47.0 %
Average value: 46.0 % Grade Count:4
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
Average value: 1.00e+16 ohm-cm Grade Count:9
Dielectric Strength 19.7 - 24.0 kV/mm
500 - 610 kV/in
Average value: 21.1 kV/mm Grade Count:3
Comparative Tracking Index 600 V
600 V
Average value: 600 V Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 193 - 227 °C
380 - 440 °F
Average value: 210 °C Grade Count:8
Nozzle Temperature 200 - 227 °C
392 - 440 °F
Average value: 218 °C Grade Count:65
Melt Temperature 149 - 279 °C
300 - 534 °F
Average value: 219 °C Grade Count:177
Mold Temperature 10.0 - 80.0 °C
50.0 - 176 °F
Average value: 48.0 °C Grade Count:178
Drying Temperature 51.7 - 100 °C
125 - 212 °F
Average value: 75.3 °C Grade Count:137
Moisture Content 0.0100 - 0.100 %
0.0100 - 0.100 %
Average value: 0.0515 % Grade Count:60
Injection Pressure 2.76 - 120 MPa
400 - 17400 psi
Average value: 54.6 MPa Grade Count:153